Microstructure and pitting corrosion resistance of annealed duplex stainless steel

The transition from metastable to stable pitting was studied in 0.5 M NaCl water solution for two cast duplex stainless steels under different microstructural conditions achieved by annealing in the range from 900 degrees C to 1200 degrees C. The ensuing microstructural changes in heat treated steels were defined and correlated with established pitting potentials (E-p) and sites of corrosion damage initiation. The variations in E-p have been discussed in terms of secondary phases precipitation. The critical condition for pit stability was quantified and used to select an appropriate microstructural state, resulting in the higher potential at which stable pit growth is first observed. (c) 2006 Elsevier Ltd. All rights reserved.