Biomimetic approaches to tendon repair

The linear organization of collagen fibers in tendons results in optimal stiffness and strength at low strains under tensile load. However, this organization makes repairing ruptured or lacerated tendons extremely difficult. Current suturing techniques to join split ends of tendons, while providing sufficient mechanical strength to prevent gapping, are inadequate to carry normal loads. Immobilization protocols necessary to restore tendon congruity result in scar formation at the repair site and peripheral adhesions that limit excursion. These problems are reviewed to emphasize the need for novel approaches to tendon repair, one of which is the development of biontimetic tendons. The objective of the empirical work described here was to produce biologically-based, biocompatible tendon replacements with appropriate mechanical properties to enable immediate mobilization following surgical repair., Nor-dihydroguaiaretic acid (NDGA), a di-catechol from creosote bush, caused a dose dependent increase in the material properties of reconstituted collagen fibers, achieving a 100-fold increase in strength and stiffness over untreated fibers. The maximum tensile strength of the optimized NDGA treated fibers averaged 90 MPa; the elastic modulus of these fibers averaged 580 MPa. These properties were independent of strain rates ranging from 0.60 to 600 mm/min. Fatigue tests established that neither strength nor stiffness were affected after 80 k cycles at 5% strain. Treated fibers were not cytotoxic to tendon fibroblasts. Fibroblasts attached and proliferated on NDGA treated collagen normally. NDGA fibers did not elicit a foreign body response nor did they stimulate an immune reaction during six weeks in vivo. The fibers survived 6 weeks with little evidence of fragmentation or degradation. The polymerization scheme described here produces a fiber-reinforced NDGA polymer with mechanical properties approaching an elastic solid. The strength, stiffness and fatigue properties of the NDGA treated fibers are comparable to those of tendon. These fibers are biocompatible with tendon fibroblasts and elicit little rejection or antigenic response in vivo. These results indicate that NDGA polymerization may provide a viable approach for producing collagenous materials that can be used to bridge gaps in ruptured or lacerated tendons. The tendon-like properties of the NDGA fiber would allow early mobilization after surgical repair. We predict that timely loading of parted tendons joined by this novel biomaterial will enhance mechanically driven production of neotendon by the colonizing fibroblasts and result in superior repair and rapid return to normal properties. (C) 2002 Elsevier Science Inc. All rights reserved.