Fatigue life estimation based on fracture mechanics of single spot welded joints under different loading modes

被引：14

作者：

Tanegashima, Ryota ^{[1
]}

Akebono, Hiroyuki ^{[2
]}

Sugeta, Atsushi ^{[2
]}

机构：

[1] Kobelco Res Inst Inc, Mech & Chem Proc Engn Div, Nishi Ku, 1-5-5 Takatsukadai, Kobe, Hyogo 6512271, Japan

[2] Hiroshima Univ, Dept Mech Sci & Engn, 1-4-1 Kagamiyama, Higashihiroshima, Hiroshima 7398527, Japan

来源：

ENGINEERING FRACTURE MECHANICS | 2017年 / 175卷

关键词：

Fracture mechanics; Stress intensity factors; Mixed-mode fracture; Welded or bonded joints; INTENSITY FACTOR SOLUTIONS; GEOMETRIC FUNCTIONS; STRESS INTENSITIES; PREDICTION; MICROSTRUCTURE; PERFORMANCE; DESIGN;

D O I：

10.1016/j.engfracmech.2017.01.031

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

To evaluate the accuracy of joint fatigue life estimations obtained using conventional theories, the fatigue properties of shear- and peel-type single spot welded joints were investigated experimentally and analytically. The observed crack initiation angles differed from the predictions obtained using conventional theories, indicating that the theories cannot be used to evaluate the fatigue properties of the joints. In contrast, the present analytical crack initiation angles were in good agreement with the experimental results. Therefore, the effect of the loading mode on the fatigue properties of the single spot welded joints was adequately determined from the range Delta K-I,K-theta max of initial stress intensity factors thorough an analytical evaluation. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：115 / 126

页数：12

共 50 条

[1] Fracture mechanics based estimation of fatigue lives of laser welded joints
Goyal, Rakesh
Bogdanov, Sergey
El-zein, Mohamad
Glinka, Grzegorz
[J]. ENGINEERING FAILURE ANALYSIS, 2018, 93 : 340 - 355
[2] Fracture mechanics-based estimation of fatigue lives of welded joints
R. Goyal
G. Glinka
[J]. Welding in the World, 2013, 57 : 625 - 634
[3] Fracture mechanics-based estimation of fatigue lives of welded joints
Goyal, R.
Glinka, G.
[J]. WELDING IN THE WORLD, 2013, 57 (05) : 625 - 634
[4] Failure modes of single resistance spot welded joints subjected to combined fatigue loading
Barkey, ME
Kang, H
Lee, YL
[J]. INTERNATIONAL JOURNAL OF MATERIALS & PRODUCT TECHNOLOGY, 2001, 16 (6-7): : 510 - 527
[5] Fracture Mechanics Based Analysis of the Fatigue Life of Defective Welded Joints
Gajdos, Lubomir
Sperl, Martin
[J]. MATERIALS TRANSACTIONS, 2020, 61 (05) : 926 - 934
[6] A simple fracture mechanics estimation of the fatigue endurance of welded joints
Chapetti, Mirco D.
Steimbreger, Ceferino
[J]. INTERNATIONAL JOURNAL OF FATIGUE, 2019, 125 : 23 - 34
[7] ANALYSIS OF FATIGUE LIFE OF WELDED-JOINTS BASED ON FRACTURE-MECHANICS
GUHA, B
PATHAK, SD
RADHAKRISHNAN, VM
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1988, 41 (04): : 315 - 318
[8] Investigation of Fatigue Crack Propagation in Spot-Welded Joints Based on Fracture Mechanics Approach
S. Hassanifard
M. A. Mohtadi Bonab
Gh. Jabbari
[J]. Journal of Materials Engineering and Performance, 2013, 22 : 245 - 250
[9] Investigation of Fatigue Crack Propagation in Spot-Welded Joints Based on Fracture Mechanics Approach
Hassanifard, S.
Bonab, M. A. Mohtadi
Jabbari, Gh
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (01) : 245 - 250
[10] Fatigue damage parameter of spot welded joints under proportional loading
Kang, HT
[J]. INTERNATIONAL JOURNAL OF AUTOMOTIVE TECHNOLOGY, 2005, 6 (03) : 285 - 291

← 1 2 3 4 5 →