Mechanical Properties and Rheological Behavior of Dynamically Vulcanized Trans-Polyisoprene/Polypropylene Blends

The degree of dynamic vulcanization, mechanical properties, rheological behavior, and the ageing-resistant performance of thermoplastic vulcanizates (TPVs) based on Trans 1,4-polyisoprene/polypropylene (TPI/PP) blends with the blend ratios of 70/30, 60/40, and 50/50 were investigated. The results showed that TPI fully dynamically vulcanized in the Haake mixer chamber when mixed with PP, and the specimen with the blend ratio 70/30, for the same sulfur content in all samples, had the lowest cross-linking degree of the TPI phase. The shear viscosity of TPI/PP-TPVs dropped as the shear rate increased and the specimen with the blend ratio 70/30 had a relatively greater shear viscosity in the region of shear rates less than 1000 s(-1). With the antiageing agent Vulkanox 4020 NA (Bayer) added, all the TPI/PP-TPVs showed good ageing characteristics, and the specimen with the blend ratio 70/30 possessed the best mechanical properties.