Mechanical alloying of fine structured Ti-Al-Nb aluminides involving Ti-hydride

被引：1
|
作者：
Bououdina, M [1 ]
Luklinska, Z [1 ]
Guo, ZX [1 ]
机构：
[1] Queen Mary Univ London, Dept Mat, London E1 4NS, England
来源：
METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, ISMANAM-2000 | 2001年 / 360-3卷
关键词：
aluminide; amorphization; mechanical alloying; Ti2AlNb; TiH2;
D O I：
10.4028/www.scientific.net/MSF.360-362.421
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to produce high-quality aluminide alloys, a comparative study was carried out on the Mechanical Alloying (MA) characteristics of two powder mixtures, Ti-22Al-23Nb and TiH2- 22Al-23Nb(at.%), respectively. It was noted that for the Ti-22Al-23Nb mixture MA led to the formation of a bcc (Nb,Ti,Al) solid solution with some degree of amorphisation under the experimental conditions. The use of Ti-hydride in the TiH2-22Al-23Nb mixture led to the formation of an amorphous (Nb,Ti,Al)H-2 solid solution. The presence of hydrogen in the powder mixture largely enhances the amorphisation process. TEM diffraction patterns confirmed the formation of both solid solutions. EDS analysis showed that chemical compositions of the bce and of the amorphous solid solutions were close to the starting values.
引用
收藏
页码：421 / 426
页数：6
相关论文
共 50 条
  • [1] Minimization of nitride formation during mechanical alloying of Ti-Al-Nb
    Biancaniello, FS
    Gayle, FW
    Suryanarayana, C
    Froes, FH
    METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2, 1996, 225 : 483 - 487
  • [2] SYNTHESIS OF B2-PHASE IN TI-AL-NB ALLOYS BY MECHANICAL ALLOYING
    CHEN, GH
    SURYANARAYANA, C
    FROES, FH
    SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (11): : 2537 - 2540
  • [3] Structure of Ti-Al-Nb intermetallics produced by mechanical alloying and hot-pressing techniques
    Dutkiewicz, J
    Maziarz, W
    Heinrich, H
    Kostorz, G
    MATERIALS CHEMISTRY AND PHYSICS, 2003, 81 (2-3) : 414 - 416
  • [4] The friction and wear properties of Ti-Al-Nb intermetallics by plasma surface alloying
    Wu, Hongyan
    Zhang, Pingze
    Li, Jianliang
    Hussain, G.
    Xu, Zhong
    TRIBOLOGY LETTERS, 2008, 30 (01) : 61 - 67
  • [5] Characterization of the invariant reaction involving the L, η, γ and σ phases in the Ti-Al-Nb system
    Rios, Orlando
    Cupid, Damian M.
    Seifert, Hans J.
    Ebrahimi, Fereshteh
    ACTA MATERIALIA, 2009, 57 (20) : 6243 - 6250
  • [6] Effect of Microstructure on Mechanical Properties of Ti-Al-Nb Ternary Alloys
    Ding Xiaofei
    Zeng Baoqing
    Xie Zhongdong
    Lin Aiguang
    Tan Yi
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (01) : 38 - 41
  • [7] THE FLOW AND FRACTURE OF A TI-AL-NB ALLOY
    LUKASAK, D
    KOSS, DA
    JOURNAL OF METALS, 1987, 39 (10): : A39 - A39
  • [8] Study of the Ti-Al-Nb phase diagram
    Kazantseva, N. V.
    Lepikhin, S. V.
    PHYSICS OF METALS AND METALLOGRAPHY, 2006, 102 (02): : 169 - 180
  • [9] Effect of alloying elements and heat treatment on the fracture toughness of Ti-Al-Nb alloys
    Kamat, S.V.
    Gogia, A.K.
    Banerjee, D.
    Acta Materialia, 1997, 46 (01): : 239 - 251
  • [10] Microstructure and mechanical properties of orthorhombic alloys in the Ti-Al-Nb system
    Gogia, AK
    Nandy, TK
    Banerjee, D
    Carisey, T
    Strudel, JL
    Franchet, JM
    INTERMETALLICS, 1998, 6 (7-8) : 741 - 748
12345