The study of electrochemical synthesis, properties and composite mechanism of PANI/PVA and PANI/PVA/Ag composite films

Purpose - The purpose of this paper is to improve the conductivity and processability of polyaniline (PANI). Design/methodology/approach - The study opted for synthesis of the conductive PANI/polyvinyl alcohol (PVA) composite film, co-doped with 5-sulphosalicylic acid and sulphuric acid. Using an electrochemical method, a small amount of silver (Ag) was electrodeposited on the film. The PVA/PANI and PVA/PANI/Ag composite films were characterised by scanning electron microscope, X-ray diffraction and infrared. The composite deposition mechanism of the composite film was investigated by cyclic voltammetry for the first time. Findings - The conductivity of the optimum PVA/PANI composite film reached 21.2 S center dot cm(-1). Then, a small amount of Ag was deposited on the PVA/PANI film, and the conductivity significantly increased by 1250 S center dot cm(-1). Through appropriate degree of stretching, the conductivity of the films was enhanced. The results indicate that uniform PVA/PANI fibres and dendritic Ag can combine to form complete three-dimensional conductive networks that exhibit better conductivity and mechanical properties. The cyclic voltammetry curves reveal that the dedoping potential of PANI was more negative than the reduction potential of Ag. Therefore, the procedure for the deposition of Ag on the PANI/PVA composite film cannot decrease the conductivity. Practical implications - This paper for the first time described and revealed the effective and practical synthesis approach and composite mechanism to prepare multi-types metal-conductive polymer composites and improve the conductivity of a conductive polymer with a less expense and one-step electrochemical method. Originality/value - This paper first explored galvanostatic oxidation to synthesise a PANI composite film to resolve the processability and conductivity of PANI by co-doped with mixed acids and deposited Ag on film. Furthermore, for the first time, the composite mechanism of metal and conductive polymer was studied.