Hydrogen assisted cracking of 2205 duplex stainless steel in synthetic sea water

被引：2
|
作者：
Michalska, J. [1 ]
Labanowski, J. [3 ]
Cwiek, J. [2 ]
机构：
[1] Silesian Tech Univ, Dept Mat Sci, Krasinskiego 8, PL-40019 Katowice, Poland
[2] Silesian Tech Univ, Inst Engn Mat & Biomat, Krasinskiego 8, PL-40019 Katowice, Poland
[3] Gdansk Univ Technol, Dept Mat & Welding Engn, PL-80952 Gdansk, Poland
来源：
TECHNOLOGIES AND PROPERTIES OF MODERN UTILISED MATERIALS (TPMUM 2012) | 2012年 / 35卷
关键词：
EMBRITTLEMENT;
D O I：
10.1088/1757-899X/35/1/012013
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The cracking behavior of 2205 duplex stainless steels (DSSs) in synthetic sea water under cathodic polarization condition was investigated. (SSRT) method was employed in aim to evaluate the susceptibility to hydrogen assisted cracking. The results showed that the reduction in the uniform elongation (UEL) and the reduction of area (RA) varied with the applied cathodic current density. Significant reductions in ductility were found, indicating its susceptibility to hydrogen-assisted fracture at current density of 10 mA cm(-2). Fractographical examinations showed that increase in hydrogenation current density cause an increase in brittle character on the fracture surface. Complete brittle fractures were observed after SSRT at10 and 20 mA cm(-2).
引用
收藏
页数：6
相关论文
共 50 条
  • [1] EVALUATION OF THE SUSCEPTIBILITY OF DUPLEX STAINLESS STEEL 2205 TO HYDROGEN ASSISTED CRACKING IN REAC SYSTEMS
    He, Mei
    Lippold, John
    Alexandrov, Boian
    Penso, Jorge
    [J]. PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2016, VOL 6B, 2017,
  • [2] Hydrogen-enhanced cracking of 2205 duplex stainless steel
    Tsay, L. W.
    Young, M. C.
    Shin, C. -S.
    Chan, S. L. I.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (12) : 1228 - 1236
  • [3] Hydrogen-enhanced cracking of 2205 duplex stainless steel welds
    Young, MC
    Chan, SLI
    Tsay, LW
    Shin, CS
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2005, 91 (01) : 21 - 27
  • [4] FACTORS AFFECTING THE ENVIRONMENTAL ASSISTED CRACKING BEHAVIOR OF 2205 DUPLEX STAINLESS STEEL
    Chasse, Kevin R.
    Yang, Di
    Singh, Preet M.
    Neu, Richard W.
    [J]. TMS 2010 139TH ANNUAL MEETING & EXHIBITION - SUPPLEMENTAL PROCEEDINGS, VOL 3: GENERAL PAPER SELECTIONS, 2010, : 401 - +
  • [5] Hydrogen Embrittlement of Duplex Stainless Steel 2205 and TiPd Alloy in a Synthetic Bentonite Pore Water
    Stoulil, Jan
    Kouril, Milan
    Carreno, Yoel Ramos
    Dobrev, David
    Gondolli, Jenny
    Nova, Katerina
    [J]. CORROSION, 2019, 75 (04) : 367 - 376
  • [6] Effect of anisotropy and slip transfer on hydrogen-assisted cracking of a 2205 duplex stainless steel: A critical analysis
    Wu, Weijie
    Fu, Hao
    Zhang, Xuewei
    Li, Weiguo
    Liu, Shenguang
    Li, Jinxu
    [J]. CORROSION SCIENCE, 2023, 213
  • [7] Hydrogen-assisted cracking in 2205 duplex stainless steel: Initiation, propagation and interaction with deformation-induced martensite
    Claeys, L.
    De Graeve, I
    Depover, T.
    Verbeken, K.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 797
  • [8] Characterization of hydrogen charging of 2205 duplex stainless steel and its correlation with hydrogen-induced cracking
    Luo, H.
    Dong, C. F.
    Liu, Z. Y.
    Maha, M. T. J.
    Li, X. G.
    [J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2013, 64 (01): : 26 - 33
  • [9] Hydrogen embrittlement of SAF 2205 duplex stainless steel
    Hsu, JW
    Tsai, SY
    Shih, HC
    [J]. CORROSION, 2002, 58 (10) : 858 - 862
  • [10] Hydrogen behavior in SAF 2205 duplex stainless steel
    Silverstein, R.
    Sobol, O.
    Boellinghaus, Th.
    Unger, W.
    Eliezer, D.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 695 : 2689 - 2695
12345