Development of a persistent superconducting joint between Bi-2212/Ag-alloy multifilamentary round wires

Superconducting joints are one of the key components needed to make Ag-alloy clad Bi2Sr2CaCu2O8+x (Bi-2212) superconducting round wire (RW) successful for high-field, high-homogeneity magnet applications, especially for nuclear magnetic resonance magnets in which persistent current mode operation is highly desired. In this study, a procedure for fabricating superconducting joints between Bi-2212 RWs during coil reaction was developed. Melting temperatures of Bi-2212 powder with different amounts of Ag addition were investigated by differential thermal analysis so as to provide information for selecting the proper joint matrix. Test joints of 1.3 mm dia. wires heat treated in 1 bar flowing oxygen using the typical partial melt Bi-2212 heat treatment (HT) had transport critical currents I-c of similar to 900 A at 4.2 K and self-field, decreasing to similar to 480 A at 14 T evaluated at 0.1 mu V cm(-1) at 4.2 K. Compared to the I-c of the open-ended short conductor samples with identical 1 bar HT, the Ic values of the superconducting joint are similar to 20% smaller than that of conductor samples measured in parallel field but similar to 20% larger than conductor samples measured in perpendicular field. Microstructures examined by scanning electron microscopy clearly showed the formation of a superconducting Bi-2212 interface between the two Bi-2212 RWs. Furthermore, a Bi-2212 RW closed-loop solenoid with a superconducting joint heat treated in 1 bar flowing oxygen showed an estimated joint resistance below 5 x 10(-12) Omega based on its field decay rate. This value is sufficiently low to demonstrate the potential for persistent operation of large inductance Bi-2212 coils.