Evolution of recrystallization microstructure and texture during rapid annealing in strip-cast non-oriented electrical steels

Non oriented electrical steel as cast strip was produced by twin roll strip casting process, and subsequently cold rolled and annealed at heating rates in the range of 3-450 degrees C/s with the aim to elucidate the effect of heating rate on the evolution of recrystallized microstructure and texture. The average grain size was rapidly increased when the heating rate was increased from 3 to 25 degrees C/s, and decreased when the heating rate was greater than 25 degrees C/s. The average grain size did not increase linearly with heating rate, which was related to different degree of nucleation and growth rate. The recrystallization texture exhibited pronounced improvement during rapid annealing. AL high heating rate, the Goss and Cube had a higher probability of nucleation of shear bands with high stored energy, while the intensity of the gamma-fiber texture was significantly reduced. The highest B-50 value attained was 1.803 Tat a heating rate of 300 degrees C/s. The study indicates that rapid heating has strong effect on the recrystallization behavior in non oriented electrical steels, which facilitates optimization of microstructure and texture, especially in the coarse grained structure. (C) 2015 Elsevier BM. All rights reserved