Effects of heat treatment on microstructure and mechanical properties of ZK60 Mg alloy

The microstructure and mechanical properties of ZK60 Mg alloy were investigated under different solution treatments and artificial aging conditions. When as-cast ZK60 alloy was solution treated at 400 degrees C for 10 h and artificially aged at 150 degrees C, the volume fraction of precipitates increased with the aging time up to 30 h. When the as-cast ZK60 alloy was solution treated at 400 degrees C for 10 h and artificially aged at 200 degrees C for 15 20 h, the volume fraction of precipitates reached a peak value. Tensile test at room temperature showed that a high density of the second phase precipitates was beneficial to improving the strength and elongation. Solution treatment at 400 degrees C for 10 h and artificial aging at 150 degrees C for 30 h is considered the optimum heat treatment condition to obtain a good combination of strength and ductility.