Provision of micro-nano bacterial cellulose as bio plastic filler by sonication method

Research and development of bioplastic has increased recently as a solution for substitution of conventional plastic which have many negative impacts to environment. However, physical properties and mechanical properties of its still lower than conventional plastic. An alternative solution for that problem is by using fillers that can increase the strength. Bacterial cellulose is considered as potential source for filler, but still need to be explored more. The privileges of bacterial cellulose are easy to get and does not have lignin, pectin, and hemicelluloses which are impurities in other celluloses. This research focused on gaining bacterial cellulose in micro-nano particle form and its impact on increasing the strength of bio plastic. Ultrasonication has been used as method to form micro-nano particle from bacterial cellulose. The result showed this method may form the particle size of bacterial cellulose approximately +/- 3 mu m. Next step, after getting +/- 3 mu m particle of bacterial cellulose, is making bio plastic with casting method by adding 1% of bacterial cellulose, from the total material in making bio plastic. Physical characteristic of the bio plastic which are tensile strength 11.85 MPa, modulus young 3.13 MPa, elongation 4.11% and density 0.42 g/cm(3). The numbers of physical properties showwthat, by adding 1% of bacterial cellulose, the strength of bio plastic was significantly increase, even value of tensile strength has complied the international standard for bio plastic.