Structures and microwave dielectric properties of Ca(1-x)Nd2x/3TiO3 ceramics

Ca(1-x)Nd2x/3TiO3 microwave dielectric ceramics were prepared by the mixed oxide route; powders were calcined at 1100 degrees C and sintered at 1450-1500 degrees C. High density, single phase products were obtained for all compositions. Grain sizes ranged from 1 mu m to 100 mu m. There was evidence of significant discontinuous grain growth in mid range compositions; all ceramics were characterised by complex domain structures. With increasing Nd content there was a evidence of a transition from an orthorhombic Pbnm structure to a monoclinic C2/m structure. This was accompanied by a decrease in relative permittivity (epsilon(r)) from 180 to 78, and decrease in the temperature coefficient of resonant frequency (tau(f)) from +770 ppm K-1 to +200 ppm K-1. The product of dielectric Q value and resonant frequency (Q x f) varied in a grossly non-systematic way, exhibiting a peak at 13,000 GHz in Ca0.7Nd0.2TiO3. (C) 2012 Elsevier Ltd. All rights reserved.