Preparation and oxidation behavior of NiCrAlYSi coating on a cobalt-base superalloy K40S

被引：45
|
作者：
Zhang, K. [1 ,2 ]
Wang, Q. M. [2 ]
Sun, C. [2 ]
Wang, F. H. [2 ]
机构：
[1] Shengyang Normal Univ, Chem & Life Coll, Shenyang 110034, Peoples R China
[2] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
CORROSION SCIENCE | 2008年 / 50卷 / 06期
基金：
中国国家自然科学基金;
关键词：
cobalt-base superalloy K40S; NiCrAlYSi coating; arc ion plating; high temperature oxidation; inter-diffusion;
D O I：
10.1016/j.corsci.2008.01.033
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Arc ion plating had been employed on a cobalt-base superalloy K40S to deposit a NiCrAlYSi coating to improve its oxidation resistance at 1323-1423 K in air. The K40S superalloy had poor oxidation resistance because a non-protective and easy spalling surface oxides scale mixed of Cr2O3 and CoCr2O4 was formed on its surface. After coated with NiCrAlYSi coating, a dense and protective alpha-Al2O3 scale was formed on the coating and excellently improved its oxidation resistance. Inter-diffusion obviously occurred between the coating and the substrate K40S superalloy in oxidation process, which resulted from Co atoms in K40S outwards diffused. A richen Cr and W carbides inter-diffusion layer was formed, which could acted as a diffusion barrier that barred Al atoms in coating inwards diffusion. Though the NiCrAlYSi changed into NiCoCrAlYSi during oxidation process, it still possessed a good oxidation resistance and. had a considerable long-term life. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1707 / 1715
页数：9
相关论文
共 50 条
  • [1] Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating
    Zhang, K.
    Liu, M. M.
    Liu, S. L.
    Sun, C.
    Wang, F. H.
    CORROSION SCIENCE, 2011, 53 (05) : 1990 - 1998
  • [2] Fatigue crack propagation behavior of K40S cobalt-base superalloy at elevated temperature
    Yang, FM
    Sun, XF
    Guan, HR
    Deng, WL
    Liu, F
    Hu, ZQ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 (01) : 50 - 54
  • [3] Fatigue crack propagation behavior of K40S cobalt-base superalloy at elevated temperature
    杨富民
    孙晓峰
    管恒荣
    邓午立
    刘芳
    胡壮麒
    Transactions of Nonferrous Metals Society of China, 2003, (01) : 50 - 54
  • [4] High-temperature low-cycle fatigue behavior of K40S cobalt-base superalloy
    F. M. Yang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Metallurgical and Materials Transactions A, 2003, 34 : 979 - 986
  • [5] High-temperature low-cycle fatigue behavior of K40S cobalt-base superalloy
    Yang, FM
    Sun, XF
    Guan, HR
    Hu, ZQ
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (04): : 979 - 986
  • [6] On the low cycle fatigue deformation of K40S cobalt-base superalloy at elevated temperature
    Yang, FM
    Sun, XF
    Guan, HR
    Hu, ZQ
    MATERIALS LETTERS, 2003, 57 (19) : 2823 - 2828
  • [7] Low cycle fatigue behavior of K40S cobalt-base superalloy at elevated temperature - II. Fatigue fractography
    Yang, FM
    Sun, XF
    Guan, HR
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2002, 38 (10) : 1053 - 1056
  • [8] Secondary M6C precipitation in K40S cobalt-base alloy
    Yang, FM
    Sun, XF
    Zhang, W
    Kang, YP
    Guan, HR
    Hu, ZQ
    MATERIALS LETTERS, 2001, 49 (3-4) : 160 - 164
  • [9] The oxidation and hot corrosion of an aluminide coating applied to a cobalt-base superalloy
    Yuan, FH
    Sun, XF
    Guan, HR
    Hu, ZQ
    INTERNATIONAL JOURNAL OF MATERIALS & PRODUCT TECHNOLOGY, 2001, : 835 - 840
  • [10] The oxidation and hot corrosion of an aluminide coating applied to a cobalt-base superalloy
    Yuan, F.H.
    Sun, X.F.
    Guan, H.R.
    Hu, Z.Q.
    International Journal of Materials and Product Technology, 2001, (SPEC ISS. VOL.2) : 835 - 840
12345