High temperature erosion behavior of plasma sprayed NiCrA1Y/WC-Co/ cenosphere coating

被引：46
|
作者：
Mathapati, Mahantayya [1 ]
Ramesh, M. R. [1 ]
Doddamani, Mrityunjay [1 ]
机构：
[1] Natl Inst Technol Karnataka, Dept Mech Engn, Surathkal, India
来源：
SURFACE & COATINGS TECHNOLOGY | 2017年 / 325卷
关键词：
Plasma spray; Cenospheres; Erosion; Brittle failure; COMPOSITE COATINGS; MILD-STEEL; HVOF; WEAR; PERFORMANCE; RESISTANCE; OXIDATION;
D O I：
10.1016/j.surfcoat.2017.06.033
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
High temperature erosive behavior of plasma sprayed NiCrAlY-25WC-Co/cenosphere coating deposited on MDN 321 steel is investigated in the present work. Coating is characterized using Scanning Electron Microscopy (SEM) and X -Ray Diffraction (XRD). Microhardness, porosity, adhesion strength, fracture toughness and ductility of the coating are quantified. Solid particle erosion test is conducted at 200, 400 and 600 C with 30 and 90 impact angles using alumina erodent. Optical profilometer is used to evaluate erosion volume loss. Erosion resistance of the coating is observed to be higher than the substrate for the test temperatures chosen and noted to be more prominent at lower impact angle and higher temperature. High temperature stability of mullite, alumina and oxide layer assists in increasing erosion resistance of coating. The eroded coating surface morphology reveals the brittle mode of material removal(C)2017 Elsevier B.V. All rights reserved.
引用
收藏
页码：98 / 106
页数：9
相关论文
共 50 条
  • [1] Cyclic Oxidation Behavior of Plasma Sprayed NiCrAlY/WC-Co/Cenosphere Coating
    Mathapati, Mahantayya
    Ramesh, M. R.
    Doddamani, Mrityunjay
    ADVANCES IN MECHANICAL DESIGN, MATERIALS AND MANUFACTURE, 2018, 1943
  • [2] High-Temperature Oxidation Behavior of NiCrA1Y Bond Coats and Stellite-6 Plasma-Sprayed Coatings
    Buta Singh Sidhu
    S. Prakash
    Oxidation of Metals, 2005, 63 : 241 - 259
  • [3] High-temperature oxidation behavior of NiCrA1Y bond coats and Stellite-6 plasma-sprayed coatings
    Sidhu, BS
    Prakash, S
    OXIDATION OF METALS, 2005, 63 (3-4): : 241 - 259
  • [4] Annealing of plasma-sprayed WC-Co coating
    Lim, LC
    Lim, SC
    Lai, MO
    Chong, SF
    Alli, S
    SURFACE & COATINGS TECHNOLOGY, 1996, 79 (1-3): : 151 - 161
  • [5] Microstructure and tribological behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere/solid lubricants composite coatings
    Doddamani, Mrityunjay
    Mathapati, Mahantayya
    Ramesh, M. R.
    SURFACE & COATINGS TECHNOLOGY, 2018, 354 : 92 - 100
  • [6] Effects of surface modification on isothermal oxidation behavior of HVOF-sprayed NiCrA1Y coatings
    Li-yong NI
    ProgressinNaturalScience:MaterialsInternational, 2011, 21 (02) : 173 - 179
  • [7] Sliding wear behavior of the supersonic plasma sprayed WC-Co coating in oil containing sand
    Du, Lingzhong
    Xu, Binshi
    Dong, Shiyun
    Zhang, Weigang
    Zhang, Jingmin
    Yang, Hua
    Wang, Haijun
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (15): : 3709 - 3714
  • [8] Sliding wear behavior of plasma sprayed 65% (NiCrSiFeBC)-35% (WC-Co) coating at elevated temperatures
    Singh, Gagandeep
    Kaur, Manpreet
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY, 2020, 234 (09) : 1396 - 1415
  • [9] High-temperature wear behaviour of HVOF sprayed 65% (NiCrSiFeBC)-35% (WC-Co) coating
    Singh, Gagandeep
    Kaur, Manpreet
    SURFACE ENGINEERING, 2020, 36 (11) : 1139 - 1155
  • [10] High efficiency chemical assisted nanofinishing of HVOF sprayed WC-Co coating
    Ghosh, Gourhari
    Sidpara, Ajay
    Bandyopadhyay, P. P.
    SURFACE & COATINGS TECHNOLOGY, 2018, 334 : 204 - 214
12345