In-situ TEM observations of dislocations motion in stoichiometric NiAl single crystals

被引:0
|
作者
Ghosh, B [1 ]
Crimp, MA [1 ]
机构
[1] Michigan State Univ, Dept Mat Sci & Mech, E Lansing, MI 48824 USA
关键词
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In an attempt to understand the relationship between dislocation mobility and the observed changes in ductility with heat treatment and alloy purity, in-situ straining TEM experiments have been carried out. Single crystals of high and commercial purity, with different orientations and thermal histories, were used in the present investigation. In all the samples dislocation motion was readily observed. The pre-existing dislocations were sessile while the newly generated dislocations glide in slip bands. Dislocations were generated both from the foil edge and the foil interior. Cross-slip was noticed in [110] and [001] oriented single crystals. These orientations also exhibited loop and debris formation after limited deformation. Dislocation motion occurred by rapid jumps in the high purity materials whereas the dislocations moved in a slow, regular manner in the commercially pure materials.
引用
收藏
页码:349 / 359
页数:11
相关论文
共 50 条
  • [1] TEM in-situ study of dislocation motion in B2 NiAl single crystals
    Ghosh, B
    Crimp, MA
    [J]. HIGH-TEMPERATURE ORDERED INTERMETALLIC ALLOYS VII, 1997, 460 : 467 - 472
  • [2] IN-SITU TEM OBSERVATIONS OF HELIUM BUBBLE INTERACTIONS WITH DISLOCATIONS
    WRIGHT, RN
    VANSICLEN, CD
    [J]. JOURNAL OF NUCLEAR MATERIALS, 1993, 206 (01) : 87 - 93
  • [3] TEM IN-SITU STRAINING OF NIAL
    NAGPAL, P
    BAKER, I
    HORTON, JA
    [J]. INTERMETALLICS, 1994, 2 (01) : 23 - 29
  • [4] Dislocations at ductile/plastic crack tips: in-situ TEM observations
    Jagannadham, K
    Wilsdorf, HGF
    Weertman, J
    [J]. MATERIALS RESEARCH INNOVATIONS, 1998, 1 (04) : 254 - 264
  • [5] Formation of dislocations in NiAl single crystals studied by in situ electrical resistivity measurement
    Sun, YQ
    Hazzledine, PM
    Dimiduk, DM
    [J]. ELECTRICALLY BASED MICROSTRUCTURAL CHARACTERIZATION II, 1998, 500 : 49 - 54
  • [6] In-situ TEM deformation studies of dislocation generation and motion in high-purity Mo single crystals
    Jouiad, M
    Lagow, BW
    Robertson, IM
    Lassila, DH
    [J]. MULTISCALE PHENOMENA IN MATERIALS-EXPERIMENTS AND MODELING, 2000, 578 : 113 - 118
  • [7] In-situ deformation of TiAlPST crystals in TEM
    Yao, KF
    Xiao, JZ
    Zhang, JL
    [J]. INTERMETALLICS, 2000, 8 (5-6) : 569 - 573
  • [8] STRESS ASYMMETRY OF STOICHIOMETRIC NIAL SINGLE-CRYSTALS
    TAKASUGI, T
    KISHINO, J
    HANADA, S
    [J]. ACTA METALLURGICA ET MATERIALIA, 1993, 41 (04): : 1021 - 1031
  • [9] Preparation, deformation and fracture of stoichiometric NiAl single crystals
    Loser, W
    Kothe, A
    Vaerst, G
    Guth, A
    [J]. HIGH-TEMPERATURE ORDERED INTERMETALLIC ALLOYS VII, 1997, 460 : 407 - 412
  • [10] In-situ observation of stress-induced stochastic twin boundary motion in off stoichiometric NiMnGa single crystals
    Barabash, Rozaliya I.
    Kirchlechner, Christoph
    Robach, Odile
    Ulrich, Olivier
    Micha, Jean-Sebastien
    Sozinov, Alexei
    Barabash, Oleg M.
    [J]. APPLIED PHYSICS LETTERS, 2013, 103 (02)