Design and development of powder processed Fe-P based alloys

The present investigation deals with designing Fe, Fe-P binary and Fe-P-Si ternary alloys produced by an in-house developed powder metallurgical technique based on 'Hot Powder Preform Forging'. Proper soaking of preforms at high temperature (1050 degrees C) eliminates iron-phosphide eutectic and brings entire phosphorus into solution in iron. Attempting hot forging thereafter completely eliminates hot as well as cold shortness and thereby helps to form these preforms (alloys) into very thin sheets of 0.5 mm. The use of costly hydrogen atmosphere during sintering has been eliminated by the addition of carbon as a reducing agent to form CO gas within the compact by reacting with oxygen of iron powder particles. The glassy ceramic coating applied over the compact serves as a protective coating to avoid atmospheric oxygen attack over the compact held at high temperature. These alloys so formed were subjected to density examination at various stages. Microstructural study has been carried out to estimate the grain size, volume percentage of porosity in the alloys, and uniform distribution of phosphorus and silicon in an iron matrix. X-ray diffraction studies of these alloys revealed the presence of only ferrite as product phase. Addition of alloying elements such as P and Si has improved the resistivity and magnetic properties of iron. Fe-0.07C-0.2O-0.3P-0.5Si alloy showed a resistivity as high as 31.7 mu Omega cm. Coercivity values of the alloys ranged from 0.51 to 1.98 Oe. The total magnetic loss of Fe-0.07C-0.2O-0.3P-0.5Si alloy was the lowest (2.03 W/kg) amongst the alloys developed owing to its high resistivity combined with its low coercivity. These alloys which are drawn to thin sheets could find their possible application in the manufacturing of transformer cores. (C) 2011 Elsevier Ltd. All rights reserved.