Analysis of a Turbine Blade Failure in a Military Turbojet Engine

This paper deals with failure analysis of a low-pressure turbine blade of a straight flow turbojet engine. The blade is made of a wrought precipitation hardened Nickel base superalloy with oxidation-resistant diffusion aluminizing coating. The failure mode is found to be fatigue with multiple cracks inside the blade having crack origin at metal carbides. In addition to the damage in the coating, carbide banding has been observed in few blades. Carbide banding may be defined as inclusions in the form of highly elongated along deformation direction. The size, shape and banding of carbides and their location critically affect the failure of blades. Carbon content needs to be optimized to reduce interdendritic segregation and thereby provide improved fatigue and stress rupture life. Hence, optimization of size, shape and distribution of carbides in the billet and forging parameters during manufacturing of blade play a vital role to eliminate/reduce extent of banding. Reference micrographs as acceptance criteria are essential for evaluation of raw material and blade. There is a need to define the acceptance criteria for carbide bandings and introduce more sensitive ultrasonic check during billet and on finished blade inspection.