Effect of Arc Welding Processes on the Weld Attributes of Type 316LN Stainless Steel Weld joint

The present study aims at understanding the effect of various arc welding processes on the evolution of microstructure, mechanical properties, residual stresses and distortion in 9 mm thick type 316LN austenitic stainless steel weld joints. Weld joints of type 316LN stainless steel were fabricated by three different arc welding processes which were commonly employed in the nuclear industry. All the weld joints passed radiographic examination. Microstructural characterization was done using optical and scanning electron microscope. Volume fraction of delta-ferrite was lowest in the A-TIG weld joint. The A-TIG welded joint exhibited adequate strength and maximum impact toughness values in comparison to that of weld joints made by SMAW and FCAW processes. The A-TIG weld joint was found to exhibit lowest residual stresses and distortion compared to that of other welding processes. This was attributed to lower weld metal volume and hence reduced shrinkage in the A-TIG weld joint compared to that of weld joints made by FCAW and SMAW processes which involved v-groove with filler metal addition. Therefore, type 316LN stainless steel A-TIG weld joint consisting of lower delta-ferrite, adequate strength, high impact toughness, lower residual stresses and distortion was suited better for elevated temperature service compared to that of SMAW and FCAW weld joints.