Effect of electrolytic hydrogen charging on the content of alloying elements in steel

被引：0

作者：

Latyshev, AA ^{[1
]}

Suranov, GI ^{[1
]}

机构：

[1] Ukhta State Engn Univ, Ukhta, Russia

来源：

METAL SCIENCE AND HEAT TREATMENT | 2003年 / 45卷 / 3-4期

关键词：

Hydrogen; Magnetic Field; Surface Layer; Fluorescent Analysis; Steel Specimen;

D O I：

10.1023/A:1024519605455

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Long-term electrolytic hydrogen charging (for up to 30 h) causes failure of steel specimens (40KhNMA) and formation of branched dendrite precipitates. Results of x-ray spectral fluorescent analysis of the variation of the content of alloying elements in the specimens, in the precipitates, and in other samples, and measured data on the mass of the specimens and on the density of the steel before and after hydrogen charging are presented. The processes of diffusion of elements under the action of active hydrogen in the surface layer of steel specimens are analyzed. Special features of hydrogen charging under the action of a constant magnetic field are considered.

引用

页码：112 / 116

页数：5

共 50 条

[1] Effect of Electrolytic Hydrogen Charging on the Content of Alloying Elements in Steel
A. A. Latyshev
G. I. Suranov
Metal Science and Heat Treatment, 2003, 45 : 112 - 116
[2] Hydrogen absorption and desorption in steel by electrolytic charging
Mertens, G.
Duprez, L.
De Cooman, B. C.
Verhaege, M.
THERMEC 2006 SUPPLEMENT: 5TH INTERNATIONAL CONFERENCE ON PROCESSING AND MANUFACTURING OF ADVANCED MATERIALS, 2007, 15-17 : 816 - 821
[3] Determination of the hydrogen fugacity during electrolytic charging of steel
Liu, Qian
Atrens, Aleks D.
Shi, Zhiming
Verbeken, Kim
Atrens, Andrej
CORROSION SCIENCE, 2014, 87 : 239 - 258
[4] Determination of the hydrogen fugacity during electrolytic charging of steel
Atrens, A. (Andrejs.Atrens@uq.edu.au), 1600, Elsevier Ltd (87):
[5] Determination of the hydrogen fugacity during electrolytic charging of steel
Atrens, Andrej (Andrejs.Atrens@uq.edu.au), 1600, Elsevier Ltd (87):
[6] Effect of Cold Working on Hydrogen Absorption and Embrittlement of Steel during Electrolytic Hydrogen Charging.
Grubitsch, H.
Binder, L.
Werkstoffe und Korrosion, 1974, 25 (08): : 565 - 570
[7] Mechanism of the inhibiting effect of pyridine derivatives on acid corrosion and electrolytic hydrogen charging of steel
Ekilik, V.V., 1600, (24):
[8] MECHANISM OF THE INHIBITING EFFECT OF PYRIDINE-DERIVATIVES ON ACID CORROSION AND ELECTROLYTIC HYDROGEN CHARGING OF STEEL
EKILIK, VV
MAKHANKO, AI
SOVIET MATERIALS SCIENCE, 1988, 24 (04): : 367 - 369
[9] EFFECT OF ALLOYING ELEMENTS ON CARBON ACTIVITY AND HYDROGEN ATTACK IN CR-MO STEEL
SAITO, Y
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1547 - 1547
[10] EFFECT OF ALLOYING ELEMENTS ON PUNCHABILITY OF STEEL SHEET
YASHIKI, H
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1410 - 1410

← 1 2 3 4 5 →