Phenyl Vinylsulfonate, a Novel Electrolyte Additive to Improve Electrochemical Performance of Lithium-Ion Batteries

Irreversible capacity fading, originating from the formation of the solid electrolyte interphase (SEI), is a common challenge encountered in lithium-ion batteries (LIBs) containing an electrolyte based on ethylene carbonate (EC). In this research, phenyl vinyl sulfonate (PVS) is examined as a novel electrolyte additive to mitigate this issue and subsequently enhance the cyclic stability of LIBs. As evidenced by density functional theory (DFT) calculations, PVS has a higher reduction potential than that of EC, which is in accordance with the cyclic voltammetry (CV) measurements. Accordingly, the PVS-containing electrolyte demonstrated a reduction peak at similar to 1.9 V, which was higher than that of the electrolyte without an additive (at similar to 1.7 V). In contrast to the SEI derived from the reference electrolyte, the one built-in PVS-containing electrolyte was capable of completely inhibiting the electrolyte reduction. In terms of the Raman spectroscopy and electrochemical impedance spectroscopy (EIS) analysis, SEI formation as the result of PVS reduction can lead to less structural disorder in the graphite electrode; the battery with the additive showed less interfacial and charge transfer resistance. The Li/graphite cell with 1 wt % of PVS delivered capacity retention much higher than that of its counterpart without the additive after 35 cycles at 1 C.