Anisotropic deformation of Zr ion irradiated Zr-2.5%Nb micro-pillars at 25 °C

被引：7
|
作者：
Oviasuyi, Richard O. [1 ]
Klassen, Robert J. [1 ]
机构：
[1] Univ Western Ontario, Dept Mech & Mat Engn, London, ON N6A 5B9, Canada
来源：
JOURNAL OF NUCLEAR MATERIALS | 2012年 / 421卷 / 1-3期
基金：
加拿大自然科学与工程研究理事会;
关键词：
PRESSURE TUBE MATERIAL; MECHANICAL-PROPERTIES; NEUTRON-IRRADIATION; PLASTIC ANISOTROPY; SIZE DEPENDENCE; YIELD LOCI; NB ALLOY; BEHAVIOR; COMPRESSION; REDUCTION;
D O I：
10.1016/j.jnucmat.2011.11.054
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Micro-pillars of 5 mu m diameter and 5 mu m height were made from textured Zr-2.5%Nb pressure tube material and were irradiated with 8.5 MeV Zr+ to simulate neutron irradiation. The yield stress, strain hardening exponent, and degree of strain localization of the micro-pillars when tested at 25 degrees C increased with ion irradiation and the extent of increase was largest in directions containing low (0001) basal pole fraction. This suggests that Zr+ irradiation inhibits prismatic dislocation slip more than pyramidal slip in this material. (c) 2011 Elsevier B.V. All rights reserved.
引用
收藏
页码：54 / 57
页数：4
相关论文
共 50 条
  • [1] Effect of Zr+ irradiation damage and crystal orientation on the uniaxial deformation of Zr-2.5%Nb micro-pillars: part 1, deformation of single-phase αZr micro-pillars
    Khan, Md Imran
    St Lawrence, Sterling
    Klassen, Robert J.
    [J]. CANADIAN METALLURGICAL QUARTERLY, 2021, 60 (01) : 28 - 40
  • [2] Effect of Zr+ implantation and crystal orientation on the uniaxial deformation of Zr-2.5%Nb micro-pillars: part 2, deformation of two-phase αΖr/βNb micro-pillars
    Khan, Md Imran
    St Lawrence, Sterling
    Klassen, Robert J.
    [J]. CANADIAN METALLURGICAL QUARTERLY, 2021, 60 (01) : 41 - 50
  • [3] Measurement and analysis of diametral deformation in irradiated Zr-2.5%Nb pressure tube
    B. N. Rath
    H. N. Singh
    J. L. Singh
    N. Kumawat
    P. M. Ouseph
    D. N. Sah
    [J]. Transactions of the Indian Institute of Metals, 2010, 63 : 671 - 674
  • [4] Measurement and analysis of diametral deformation in irradiated Zr-2.5%Nb pressure tube
    Rath, B. N.
    Singh, H. N.
    Singh, J. L.
    Kumawat, N.
    Ouseph, P. M.
    Sah, D. N.
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2010, 63 (2-3) : 671 - 674
  • [5] Temperature dependence of the anisotropic deformation of Zr-2.5%Nb pressure tube material during micro-indentation
    Bose, B.
    Klassen, R. J.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2011, 419 (1-3) : 235 - 240
  • [6] Effect of ion irradiation and indentation depth on the kinetics of deformation during micro-indentation of Zr-2.5%Nb pressure tube material at 25 °C
    Bose, B.
    Klassen, R. J.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2010, 399 (01) : 32 - 37
  • [7] Evolution of Interphase Stress in Zr-2.5% Nb during Deformation
    Cai, S.
    Daymond, Mark R.
    Holt, R. A.
    Oliver, E. C.
    [J]. THERMEC 2006 SUPPLEMENT: 5TH INTERNATIONAL CONFERENCE ON PROCESSING AND MANUFACTURING OF ADVANCED MATERIALS, 2007, 15-17 : 615 - 620
  • [8] EXAMINATION OF EXPLOSIVE WELDED ZR-2.5 NB/STEEL AND ZR-2.5 NB/STAINLESS STEEL JOINTS
    BEGHI, G
    SCHAUER, G
    [J]. ENERGIA NUCLEARE, 1971, 18 (7-8): : 421 - &
  • [9] Computation of diametral deformation of irradiated Zr-2.5 Nb pressure tubes from RAPS-2
    S. Chatterjee
    Priti Kotak Shah
    J. S. Dubey
    [J]. Transactions of the Indian Institute of Metals, 2010, 63 : 369 - 372
  • [10] Computation of diametral deformation of irradiated Zr-2.5 Nb pressure tubes from RAPS-2
    Chatterjee, S.
    Shah, Priti Kotak
    Dubey, J. S.
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2010, 63 (2-3) : 369 - 372
12345