Effect of 1 wt% LiF additive on the densification of nanocrystalline Y2O3 ceramics by spark plasma sintering

被引：49

作者：

Marder, Rachel ^{[1
]}

Chaim, Rachman ^{[1
]}

Chevallier, Geoffroy ^{[2
]}

Estournes, Claude ^{[2
]}

机构：

[1] Technion Israel Inst Technol, Dept Mat Engn, IL-32000 Haifa, Israel

[2] CNRS, Inst Carnot Cirimat, F-31602 Toulouse 9, France

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2011年 / 31卷 / 06期

关键词：

Grain growth; Sintering; Grain size; Yttrium oxide; MGAL2O4; SPINEL; TRANSPARENT; MGO; PRESSURE; SPS; MICROSTRUCTURE; FABRICATION; MECHANISM; ALUMINA; YTTRIA;

D O I：

10.1016/j.jeurceramsoc.2010.12.032

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Densification of nanocrystalline cubic yttria (nc-Y2O3) powder, with 18 nm crystal size and 1 wt% LiF as a sintering additive was investigated. Specimens were fabricated by spark plasma sintering at 100 MPa, within the temperature range of 700-1500 degrees C. Sintering at 700 degrees C for 5 and 20 min resulted in 95% and 99.7% dense specimens, with an average grain size of 84 and 130 nm, respectively. nc-Y2O3 without additive was only 65% dense at 700 degrees C for 5 min. The presence of LiF at low sintering temperatures facilitated rapid densification by particle sliding and jamming release. Sintering at high temperatures resulted in segregation of LiF to the grain boundaries and its entrapment as globular phase within the fast growing Y2O3 grains. The sintering enhancement advantage of LiF was lost at high SPS temperatures. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：1057 / 1066

页数：10

共 50 条

[1] Densification of nanocrystalline Y2O3 ceramic powder by spark plasma sintering
Chaim, Rachman
Shlayer, Amit
Estournes, Claude
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2009, 29 (01) : 91 - 98
[2] Effects of Y2O3 additions on the densification and thermal conductivity of spark plasma sintering AlN ceramics
Kim, Kyoung Hun
Park, Joo Seok
Ahn, Jong Pil
Chae, Jae Hong
Lee, Byung Ha
Shim, K. B.
JOURNAL OF CERAMIC PROCESSING RESEARCH, 2009, 10 (01): : 109 - 112
[3] Spark plasma sintering of translucent polycrystalline α/β-silicon nitride ceramics with Y2O3 additive
Koroglu, Levent
Ak, Gizem
Kurama, Semra
MATERIALS CHEMISTRY AND PHYSICS, 2023, 299
[4] Effects of Y2O3 Addition on Densification and Thermal Conductivity of AIN Ceramics During Spark Plasma Sintering
Chae, Jae Hong
Park, Joo Seok
Ahn, Jong Pih
Kim, Kyoung Hun
Lee, Byung Ha
JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2008, 45 (12) : 827 - 831
[5] Superfast Sintering of Nanocrystalline Y2O3 Ceramics
Zheng, Xia
Fu, Zhengyi
Zhang, Jinyong
Wang, Weiming
Wang, Hao
Wang, Yucheng
Lee, Soo Wohn
Niihara, Koich
ADVANCED SYNTHESIS AND PROCESSING TECHNOLOGY FOR MATERIALS, 2009, 66 : 100 - +
[6] Densification of nanocrystalline TiC ceramics by spark plasma sintering
Chaim, Rachman
Kleiner, Liliya
Kalabukhov, Sergey
MATERIALS CHEMISTRY AND PHYSICS, 2011, 130 (1-2) : 815 - 821
[7] Densification of nanocrystalline NiO ceramics by spark plasma sintering
Chaim, R.
Bar-Hama, O. Reinharz
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (03): : 462 - 468
[8] Densification mechanisms in spark plasma sintering of nanocrystalline ceramics
Chaim, Rachman
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 443 (1-2): : 25 - 32
[9] Densification and polymorphic transition of multiphase Y2O3 nanoparticles during spark plasma sintering
Marder, R.
Chaim, R.
Chevallier, G.
Estournes, C.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (24): : 7200 - 7206
[10] Densification maps for spark plasma sintering of nanocrystalline MgO ceramics
Chaim, R
Margulis, M
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 407 (1-2): : 180 - 187

← 1 2 3 4 5 →