Friction and wear behaviour of steam-oxidized sintered iron components coated with manganese phosphate

被引：24
|
作者：
De Mello, Jose Daniel B.
Costa, Henara L.
Binder, Roberto
机构：
[1] Fed Univ, Lab Tribol & Mat, BR-38400901 Monica, Brazil
[2] Empersa Brasileira Compressores, BR-83219100 Joinville, SC, Brazil
来源：
WEAR | 2007年 / 263卷
关键词：
steam oxidation; manganese phosphate; sintered components; friction; sliding wear; abrasive wear;
D O I：
10.1016/j.wear.2007.01.062
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Steam oxidation is an important industrial procedure for changing tribological properties, sealing porosity and improving aesthetics in sintered iron components. Manganese phosphate coatings are believed to have intrinsic lubricant properties and very low friction coefficients. In this work, after steam oxidation, sintered iron components were coated with manganese phosphate and their tribological behaviour was investigated. Components with two nominal film thicknesses were compared, either coated or uncoated with manganese phosphate. Their abrasion resistance was evaluated using micro abrasion wear tests. Reciprocating wear tests were used to study their sliding wear resistance. It was observed that phosphating of the oxidized samples resulted in an increase of the wear rate in both tests. Phosphating promoted a reduction of the oxide film thickness, probably due to the chemical conversion reaction with the oxide substrate. The reduction of wear resistance due to phosphating was associated with a reduction of oxide film thickness. (C) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：842 / 848
页数：7
相关论文
共 50 条
  • [1] Friction and wear behavior of steam-oxidized ferrous PM compacts
    Raj, P. Philomen-D-Anand
    Palaniradja, K.
    GopalaKrishna, A.
    [J]. JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY, 2016, 30 (10) : 4535 - 4541
  • [2] Friction and wear behavior of steam-oxidized ferrous PM compacts
    P. Philomen-D-Anand Raj
    K. Palaniradja
    A. GopalaKrishna
    [J]. Journal of Mechanical Science and Technology, 2016, 30 : 4535 - 4541
  • [3] Effect of processing parameters on the surface durability of steam-oxidized sintered iron
    De Mello, JDB
    Hutchings, IM
    [J]. WEAR, 2001, 250 (PART 1) : 435 - 448
  • [4] FRICTION AND WEAR OF SINTERED IRON
    GOPINATH, K
    RAYUDU, GVN
    NARAYANAMURTHI, RG
    [J]. WEAR, 1977, 42 (02) : 245 - 250
  • [5] Evaluation of the wear process of cast iron coated with manganese phosphate
    Oyamada, T
    Inoue, Y
    [J]. TRIBOLOGY TRANSACTIONS, 2003, 46 (01) : 95 - 100
  • [6] The Investigation of Friction and Wear Characteristic of Cast Iron against Manganese Phosphate Coated and Austempered Compressor Crankshaft
    Sipcikoglu, Baris Ishak
    Yigit, Burcu
    Oflaz, Huseyin
    Parlar, Zeynep
    Temiz, Vedat
    [J]. FME TRANSACTIONS, 2015, 43 (03): : 186 - 190
  • [7] FRICTION AND WEAR BEHAVIOUR OF SINTERED BRASS
    Li Xibin
    Tan Linying
    Su Chunming
    Li Meiying(Powder Metallurgy Research Institute
    [J]. Journal of Central South University, 1994, (01) : 23 - 28
  • [8] Wear process of cast iron coated with manganese phosphate and its evaluation method
    Oyamada, T
    Inoue, Y
    [J]. JOURNAL OF JAPANESE SOCIETY OF TRIBOLOGISTS, 2002, 47 (08) : 656 - 662
  • [9] Wear process of cast iron coated with manganese phosphate and its evaluation method
    Oyamada, Tomonaga
    Inoue, Youichi
    [J]. Toraibarojisuto/Journal of Japanese Society of Tribologists, 2002, 47 (08): : 656 - 662
  • [10] Abrasive wear of steam-treated sintered iron
    da Silva, WM
    Binder, R
    de Mello, JDB
    [J]. WEAR, 2005, 258 (1-4) : 166 - 177
12345