Coupled carbonation-rust formation-damage modeling and simulation of steel corrosion in 3D mesoscale reinforced concrete

被引：48
|
作者：
Nguyen, T. T. H. [1 ]
Bary, B. [1 ]
de Larrard, T. [1 ,2 ]
机构：
[1] CEA, Lab Etud Comportement Betons & Argiles, DEN, DPC,SECR, F-91191 Gif Sur Yvette, France
[2] UPS INSA Toulouse, LMDC, Toulouse, France
来源：
CEMENT AND CONCRETE RESEARCH | 2015年 / 74卷
关键词：
Modeling; Corrosion; Finite element analysis; Carbonation; Microcracking; LONG-TERM CORROSION; REBAR CORROSION; ATMOSPHERIC CORROSION; COVER CRACKING; IRON-OXIDE; ARTIFACTS; BEHAVIOR; TEMPERATURE; DURABILITY; MECHANISMS;
D O I：
10.1016/j.cemconres.2015.04.008
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This paper presents a modeling strategy to simulate the corrosion of steel reinforcement in atmospheric environment due to carbonation of concrete. Its principal objectives are to analyze the effects of the progressive formation of corrosion products at the steel/concrete interface on concrete cover cracking. The approach is based on modeling studies carried out independently on carbonation, corrosion and creep. These models are coupled and integrated into a numerical 3D simulation procedure for investigating the behavior of concrete mesostructures. A viscodamage model is used to reproduce both creep and damage behaviors of mortar, and the approach is applied to the simulation of a 3D reinforced concrete mesostructure including explicitly the coarse aggregates. The numerical results highlight the influence of aggregates and the effects of creep on crack initiation and propagation. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：95 / 107
页数：13
相关论文
共 50 条
  • [1] A coupled carbonation- rust formation-mechanical damage model for steel corrosion in reinforced concrete
    Nguyen, T. T. H.
    Bary, B.
    DeLarrard, T.
    L'Hostis, V.
    COMPUTATIONAL MODELLING OF CONCRETE STRUCTURES, VOL 2, 2014, : 649 - 658
  • [2] 3D mesoscale simulation of the influence of corrosion on loss of tension stiffening in reinforced concrete
    Avadh, Kumar
    Jiradilok, Punyawut
    Bolander, E. John
    Nagai, Kohei
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 339
  • [3] A 3D cohesive-frictional coupled interface model for mesoscale simulation of steel fibre-reinforced concrete
    Yang, Zhenjun
    Zhang, Xin
    Wang, Zhenyu
    Li, Q. M.
    INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING, 2024, 125 (02)
  • [4] 3D simulation of localized steel corrosion in chloride contaminated reinforced concrete
    Cao, Chong
    CONSTRUCTION AND BUILDING MATERIALS, 2014, 72 : 434 - 443
  • [5] Modeling damage in concrete caused by corrosion of reinforcement: coupled 3D FE model
    Joško Ožbolt
    Filip Oršanić
    Gojko Balabanić
    Marija Kušter
    International Journal of Fracture, 2012, 178 : 233 - 244
  • [6] Modeling damage in concrete caused by corrosion of reinforcement: coupled 3D FE model
    Ozbolt, Josko
    Orsanic, Filip
    Balabanic, Gojko
    Kuster, Marija
    INTERNATIONAL JOURNAL OF FRACTURE, 2012, 178 (1-2) : 233 - 244
  • [7] 3D mesoscale investigation of non-uniform steel corrosion in reinforced concrete under chloride environments
    Zeng, Chen
    Zheng, Zhi-shan
    Zhang, Hui
    Huang, Yu-jie
    Wang, Xiang
    Liu, Gang
    CONSTRUCTION AND BUILDING MATERIALS, 2024, 411
  • [8] 3D mesoscale modelling of steel fiber-reinforced aggregate concrete
    Wu, Zhangyu
    She, Wei
    Zhang, Jinhua
    Tang, Jinhui
    Cao, Yubin
    Da, Bo
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2023, 257
  • [9] Modeling concrete reinforced with recycled and industrial steel fibers at high temperatures using 3D mesoscale analysis
    Yaghout Modarres
    Mansour Ghalehnovi
    Innovative Infrastructure Solutions, 2025, 10 (5)
  • [10] Modeling Steel Corrosion Failure in Reinforced Concrete by Cover Crack Width 3D FEM Analysis
    Castorena-Gonzalez, J. H.
    Martin, U.
    Gaona-Tiburcio, C.
    Nunez-Jaquez, R. E.
    Almeraya-Calderon, F. M.
    Bastidas, J. M.
    Bastidas, D. M.
    FRONTIERS IN MATERIALS, 2020, 7
12345