Fiber-Reinforced Cemented Paste Backfill: The Effect of Fiber on Strength Properties and Estimation of Strength Using Nonlinear Models

This experimental investigation was conducted to research the properties of polypropylene (PP) fiber-reinforced cemented paste backfill (CPB). The unconfined compressive strength (UCS) of the fiber-reinforced CPB showed a significant improvement with average UCS increase ratios of 141.07%, 57.62% and 63.17% at 3, 7 and 28 days, respectively. The macroscopic failure mode and SEM analysis indicated that fibers prevented the formation of large tensile and shear cracks during the pull-out and pull-off failure modes. A linear fitting function for the UCS at a curing time of 3 days and two polynomial fitting functions for the UCS at curing times of 7 and 28 days were established to characterize the relationship between the UCS of the fiber-reinforced and unreinforced CPB. Moreover, based on composite mechanics, nonlinear models related to the UCS and fiber reinforcement index were obtained. The estimated functions containing the fiber reinforcement index lambda, which consists of the fiber content and aspect ratio of fiber, could evaluate the UCS. Furthermore, the fiber reinforcement index lambda quantifies the enhancement by the fibers. Both estimation results indicated that the UCS values were estimated accurately at curing times of 3, 7 and 28 days in this study. Additionally, the estimation models could be used to guide the strength design of fiber-reinforced CPB. Besides this, the results showed that fiber-reinforced CPB can be used more widely in mine backfills and meets the requirements of controlled low-strength material (CLSM) for broader applications.