Effect of Zr Addition on Localized Corrosion Behavior of Al-Zn-Mg Alloy

被引：0
|
作者：
Liu, S. D. [1 ,2 ,3 ]
Chai, W. R. [1 ,2 ,3 ]
Wang, Q. [1 ,2 ,3 ]
Pan, Q. L. [1 ,2 ,3 ]
Li, A. D. [4 ]
Deng, Y. L. [1 ,2 ,3 ]
Zhang, X. M. [1 ,2 ,3 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
[2] Minist Educ, Key Lab Nonferrous Met Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
[3] Nonferrous Met Oriented Adv Struct Mat & Mfg Coop, Changsha 410083, Hunan, Peoples R China
[4] Suntown Technol Grp Co Ltd, Changsha 410200, Hunan, Peoples R China
来源：
HIGH PERFORMANCE STRUCTURAL MATERIALS | 2018年
关键词：
Aluminium; Localized corrosion; Recrystallization; STEM; MECHANICAL-PROPERTIES; MICROSTRUCTURE; CRACKING; SC;
D O I：
10.1007/978-981-13-0104-9_26
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of Zr addition on localized corrosion resistance of Al-Zn-Mg alloy were investigated by means of intergranular corrosion (IGC) immersion and exfoliation corrosion (EXCO) immersion tests. The mechanism was discussed based on microstructural characterization by optical microscopy (OM) and scanning transmission electron microscopy (STEM). The results showed that Al-Zn-Mg-Zr alloy exhibited a smaller intergranular corrosion depth and exfoliation corrosion depth than Al-Zn-Mg alloy. Zr inhibited recrystallization and refines grains. The subgrain boundaries could retard the propagation of corrosion. Compared with Al-Zn-Mg alloy, Al-Zn-Mg-Zr alloy has lower Zn and Mg content of the grain boundary precipitates and narrower precipitate free zone near grain boundaries.
引用
收藏
页码：247 / 254
页数：8
相关论文
共 50 条
  • [1] Effect of minor Ge addition on microstructure and localized corrosion behavior of Al-Zn-Mg alloy sheet
    Liu, Shengdan
    Wang, Qing
    Yang, Zhenshen
    Chai, Wenru
    Chen, Jingchao
    Ye, Lingying
    Tang, Jianguo
    MATERIALS CHARACTERIZATION, 2019, 156
  • [2] Comparative Study on the Effect of Over-aging and Addition of Zr on the Corrosion Resistance of Al-Zn-Mg Alloy
    Qu M.
    Tang J.
    Ye L.
    Li C.
    Li J.
    Zhou W.
    Deng Y.
    Cailiao Daobao/Materials Reports, 2020, 34 (01): : 02083 - 02087
  • [3] COMPARISON OF CORROSION AND STRESS CORROSION BEHAVIOR OF A TERNARY AL-ZN-MG ALLOY
    SEDRIKS, AJ
    GREEN, JAS
    MATERIALS PROTECTION, 1969, 8 (12): : 49 - &
  • [4] COMPARISON OF CORROSION AND STRESS CORROSION BEHAVIOR OF A TERNARY AL-ZN-MG ALLOY
    SEDRIKS, AJ
    GREEN, JAS
    CORROSION, 1969, 25 (12) : 6 - &
  • [5] Effect of sampling direction on the stress corrosion cracking behavior of Al-Zn-Mg alloy
    Wu J.-S.
    Deng Y.-L.
    Zhang Z.
    Zhang Y.-D.
    Sun L.
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2019, 41 (03): : 350 - 358
  • [6] EFFECT OF COPPER ADDITION ON CORROSION RESISTANCE OF COMMERCIAL Al-Zn-Mg ALLOY WELDS.
    Enjo, Toshio
    Kuroda, Toshio
    Transactions of JWRI (Japanese Welding Research Institute), 1985, 14 (01): : 77 - 82
  • [7] Effect of minor Sc addition on microstructure and stress corrosion cracking behavior of medium strength Al-Zn-Mg alloy
    Li, Zhaoming
    Jiang, Haichang
    Wang, Yunli
    Zhang, Duo
    Yan, Desheng
    Rong, Lijian
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (07) : 1172 - 1179
  • [8] COMPARISON OF CORROSION AND STRESS-CORROSION BEHAVIOR OF A TERNARY AL-ZN-MG ALLOY
    SEDRIKS, AJ
    GREEN, JAS
    NOVAK, DL
    METALLURGICAL TRANSACTIONS, 1970, 1 (07): : 1815 - &
  • [9] Effect of microstructure on exfoliation corrosion resistance in an Al-Zn-Mg alloy
    Lu, Xianghan
    Han, Xiaolei
    Du, Zhiwei
    Wang, Guojun
    Lu, Liying
    Lei, Jinqin
    Zhou, Tietao
    MATERIALS CHARACTERIZATION, 2018, 135 : 167 - 174
  • [10] Effect of flame rectification on corrosion property of Al-Zn-Mg alloy
    Li, Shuai
    Guo, Dan
    Dong, Hong-gang
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2017, 27 (02) : 250 - 257
12345