Mechanochemical synthesis of Co and Ni decorated with chemically deposited Pt as electrocatalysts for oxygen reduction reaction

High energy milling in combination with galvanic displacement were used for the preparation of bimetallic nanocatalysts. Co and Ni monometallic powders milled for 30 and 20 h, respectively were both produced in air atmosphere and used as precursors for the preparation of M-Pt (M = Co,Ni) compounds. Nanosized monometallic powders were physically supported on Vulcan carbon, and covered with 20 wt% Pt through a Galvanic Displacement Reaction (GDR) to produce Co-20Pt/C and Ni-20Pt/C electrocatalysts. XRD was used for phase identification on milled powders and for demonstrating structural transformations of Co powders during milling. Results on unmilled metallic Co powder show a predominant HCP structure modifying to a FCC structure after milling. Ni powders maintain their same FCC structure. Energy Dispersive X-Ray Spectometry (EDX) was used for chemical composition analysis on milled powders at several milling times. Scanning Transmission Electron Microscopy (STEM) show the formation of heterogeneous particle with similar to 10 nm in size for both electrocatalysts. The electrocatalytic activity was evaluated by Cyclic Voltammetry (CV) and steady state Rotating Disk Electrode (RDE) for the Oxygen Reduction Reaction (ORR) in 0.1 M HClO4. The kinetic parameters on Co-20Pt/C conducted to the highest mass activity for the cathodic reaction. (C) 2016 Elsevier B.V. All rights reserved.