Effects of PAIR (pre-annealing and intermediate rolling) process on superconducting properties of Bi2Sr2CaCu2Ox/Ag multilayer tapes

被引：35

作者：

Miao, H

Kitaguchi, H

Kumakura, H

Togano, K

Hasegawa, T

机构：

[1] Natl Res Inst Met, Tsukuba, Ibaraki 3050047, Japan

[2] Showa Elect Wire & Cable, Kawasaki, Kanagawa 2100843, Japan

来源：

PHYSICA C | 1998年 / 301卷 / 1-2期

关键词：

Bi-2212; tape conductor; critical current density; fabrication process;

D O I：

10.1016/S0921-4534(98)00170-1

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

PAIR process, which is the combination of pre-annealing (PA) and intermediate rolling (IR) processes and is performed prior to melt-solidification, enhances J(c) of the Bi-2212/Ag composite tapes. The effects of pre-annealing and intermediate rolling process on microstructure and J(c) of the Bi-2212/Ag multilayer tapes fabricated by the oxide-painting method have been studied. The results show that J(c) has been increased strongly by performing pre-annealing at 800-880 degrees C and intermediate rolling with > 25% deformation. Transport J(c) of 3.3 X 10(5) A/cm(2) in magnetic field (4.2 K, 10 T) is obtained. The enhancement of J(c) is assigned to the microstructure with high grain alignment and uniformity, as well as the improvement of grain coupling by the PAIR process. (C) 1998 Elsevier Science B.V. All rights reserved.

引用

页码：116 / 122

页数：7

共 50 条

[1] Effects of PAIR (pre-annealing and intermediate rolling) process on superconducting properties of Bi2Sr2CaCu2Ox/Ag multilayer tapes
Miao, H.
Kitaguchi, H.
Kumakura, H.
Togano, K.
Hasegawa, T.
Physica C: Superconductivity and its Applications, 1998, 301 (1-2): : 116 - 122
[2] Critical current density distribution in the superconducting oxide layer of pre-annealing and intermediate-rolling processed Bi2Sr2CaCu2Ox/Ag composite tapes
Hishinuma, Y
Kitaguchi, H
Miao, HP
Kumakura, H
Itoh, K
Togano, K
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1998, 11 (11): : 1237 - 1240
[3] Critical current density distribution in the superconducting oxide layer of pre-annealing and intermediate-rolling processed Bi2Sr2CaCu2Ox/Ag composite tapes
Tsukuba Univ, Tsukuba, Japan
Superconductor Science and Technology, 1998, 11 (11): : 1237 - 1240
[4] Bi2Sr2CaCu2Ox/Ag multilayer tapes with Jc>500 000 A/cm2 at 4.2 K and 10 T by using pre-annealing and intermediate rolling process
Miao, H.
Kitaguchi, H.
Kumakura, H.
Togano, K.
Hasegawa, T.
Koizumi, T.
Physica C: Superconductivity and its Applications, 1998, 303 (1-2): : 81 - 90
[5] Development of multilayer Bi2Sr2CaCu2Ox superconducting tapes
Hasegawa, T
Koizumi, T
Ohtani, N
Kitaguchi, H
Kumakura, H
Togano, K
Miao, H
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (01): : 23 - 28
[6] Relationship between Bi2Sr2CaCu2Ox layer thickness and Jc enhancement by pre-annealing and intermediate rolling process
Kitaguchi, H
Miao, H
Kumakura, H
Togano, K
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1999, 320 (1-2): : 71 - 76
[7] Reaction mechanism and microstructure of PAIR (per-annealing and intermediate rolling) processed Bi2Sr2CaCu2Ox/Ag tapes
Hasegawa, T
Koizumi, T
Aoki, Y
Kitaguchi, H
Miao, H
Kumakura, H
Togano, K
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 1884 - 1887
[8] Reaction mechanism and microstructure of PAIR (per-annealing and intermediate rolling) processed Bi2Sr2CaCu2Ox/Ag tapes
Hasegawa, T.
Koizumi, T.
Aoki, Y.
Kitaguchi, H.
Miao, H.
Kumakura, H.
Togano, K.
IEEE Transactions on Applied Superconductivity, 1999, 9 (2 II): : 1884 - 1886
[9] Bi2Sr2CaCu2Ox/Ag multilayer tapes with Jc>500000A/cm2 at 4.2 K and 10 T by using pre-annealing and intermediate rolling process
Miao, H
Kitaguchi, H
Kumakura, H
Togano, K
Hasegawa, T
Koizumi, T
PHYSICA C, 1998, 303 (1-2): : 81 - 90
[10] Fabrication and properties of superconducting magnets using Bi2Sr2CaCu2Ox/Ag tapes
Tomita, N
Arai, M
Yanagisawa, E
Morimoto, T
Kitaguchi, H
Kumakura, H
Togano, K
Nomura, K
CRYOGENICS, 1996, 36 (06) : 485 - 490

← 1 2 3 4 5 →