Structural and Morphological Studies on Li2Fe0.5Mn0.5SiO4/C Composite Synthesized Using Polyvinyl Alcohol for Energy Storage Devices

In this study, we first focus on effects of PVA surfactant on Li2Fe0.5Mn0.5SiO4/C by using X-ray diffraction, Fourier transform infrared spectroscopy, micro Raman analysis, scanning electron microscope, transmission electron microscope and magnetization measurements. XRD result reveals the formation of new phase (Li2Fe0.5Mn0.5SiO4/C), as a result of embedded carbon, intensity of the peaks was also suppressed. Intensity domination of G-band in micro Raman analysis affirmed that the establishment of graphene formation which was yielded from decomposition of organic materials of both PVA and acetate. Confirmation of Si-O and Si-C bond in the as- prepared material was made by FTIR analyses. A well uniform spherical shaped morphology was observed in both SEM and TEM images. In addition, the TEM picture further demonstrates Li2Fe0.5Mn0.5SiO4/C with average particle size of about 20nm by PVA introducing.