Analysis of defects in stainless steel piping

被引：0
|
作者：
Janulionis, R. [1 ]
Dundulis, G. [1 ]
Karalevicius, R. [1 ]
机构：
[1] Lithuanian Energy Inst, LT-44403 Kaunas, Lithuania
来源：
MECHANIKA | 2011年 / 06期
关键词：
D O I：
10.5755/j01.mech.17.6.999
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
This article presents the evaluation of defects detected in the austenitic stainless steel piping in the main circulation circuit of Ignalina NPP Uunit 2 during the last planned preventive maintenance in 2008. Defect evaluation procedure consists of two parts: the evaluation of defects acceptability and the second part consists of crack growth calculation. For the evaluation of defects R6 option 1 method was used. The analysis showed that all 126 detected defects during planned preventive maintenance in 2008 are in acceptable region and all the welds can be used without repairing. These piping will be used even at NPP decommission stage during decontamination procedure. Therefore the impermeability of piping should be ensured for decommissioned NPP until decontamination of the piping will be done. Evaluation of the defects in austenitic stainless steel piping should be done according to the methodology described in this article.
引用
收藏
页码：585 / 589
页数：5
相关论文
共 50 条
  • [1] Failure analysis of stainless steel piping at an offshore platform
    Velu, Balraj
    MATERIALS PERFORMANCE, 2008, 47 (05) : 62 - 65
  • [2] STAINLESS-STEEL PIPING
    TUTHILL, AH
    JOURNAL AMERICAN WATER WORKS ASSOCIATION, 1994, 86 (07): : 67 - 73
  • [3] Hydrotesting stainless steel piping
    不详
    MATERIALS PERFORMANCE, 2008, 47 (06) : 64 - 64
  • [4] EVALUATION OF THE INTER GRANULAR STRESS CORROSION CRACKING DEFECTS IN AUSTENITIC STAINLESS STEEL PIPING
    Janulionis, Remigijus
    Dundulis, Gintautas
    Karalevicius, Renatas
    ICONE17, VOL 4, 2009, : 443 - 448
  • [5] Welding stainless steel piping with no backing gas
    Messer, B
    Lawrence, G
    Oprea, V
    Patrick, C
    Phillips, T
    WELDING JOURNAL, 2002, 81 (12) : 32 - 34
  • [6] Radiography of thinwall stainless steel piping welds
    Wilson, G
    Smalley, S
    INSIGHT, 2004, 46 (01) : 23 - 25
  • [7] Welding stainless steel piping with no backing gas
    Messer, Barry
    Lawrence, Greg
    Oprea, Vasile
    Patrick, Charles
    Phillips, Terry
    Welding Journal (Miami, Fla), 2002, 81 (12): : 32 - 34
  • [8] BUTTING - Delivery and assembly of stainless steel piping
    不详
    WOCHENBLATT FUR PAPIERFABRIKATION, 2000, 128 (21): : 1458 - 1458
  • [9] Failure analysis of a welded stainless-steel piping system with premature pitting
    Bedoya-Zapata, Alvaro Diego
    Franco-Rendon, Carlos Mauricio
    Leon-Henao, Henry
    Santa, Juan Felipe
    Barrada, Jorge Enrique Giraldo
    ENGINEERING FAILURE ANALYSIS, 2021, 119
  • [10] Thermal Fatigue Testing and Analysis of Stainless Steel Girth Butt Weld Piping
    Zechmeister, M. J.
    Reinheimer, R. D.
    Jones, D. P.
    Damiani, T. M.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE VOL 1: CODES AND STANDARDS, 2012, : 651 - 669
12345