Enhancement of the tensile shear strength for joining low-ductility aluminium to high-strength steel by using electrically-assisted mechanical clinching (EAMC)

The present work studied the enhancement of the tensile shear strength for joining AA6061-T6 aluminium to galvanized DP590 steel via electrically-assisted mechanical clinching (EAMC) using an integrated 2D FE model. To defeat the difficulties of joining low-ductility aluminium alloy to high-strength steel, the electroplastic effect obtained from the electrically-assisted process was applied to enhance the clinch-ability. For this purpose, the results of experiments performed by the chamfering punches with and without electrically-assisted pre-heating were compared. Joint cross-section, failure load, failure mode, fracture displacement, material flow, and failure mechanism were assessed in order to study the failure behaviour. The results showed that the joints clinched at the EAMC condition failed with the dominant dimpled mechanism observed on the fracture surface of AA6061 side, achieved from the athermal effect of the electroplasticity. Besides, these joints were strengthened 32% with a much more fracture displacement around 20% compared with non-electrically-assisted pre-heating.