Transport properties of Bi-2212/Ag multifilamentary composite tape in high magnetic fields

被引：14

作者：

Okada, M ^{[1
]}

Tanaka, K ^{[1
]}

Fukushima, K ^{[1
]}

Sato, J ^{[1
]}

Higashiyama, K ^{[1
]}

机构：

[1] HITACHI CABLE LTD,ADV RES CTR,TSUCHIURA,IBARAKI 300,JAPAN

来源：

PHYSICA B | 1996年 / 216卷 / 3-4期

关键词：

D O I：

10.1016/0921-4526(95)00484-X

中图分类号：

O469 [凝聚态物理学];

学科分类号：

070205 ;

摘要：

Silver sheathed Bi-2212 multifilamentary tapes with 19-55 cores were successfully developed through the continuous pressing followed by a partial melting process. The multifilamentary tapes showed J(c)'s of 1800 A/mm(2) (B parallel to tape face) and 1100 A/mm(2) (B perpendicular to tape) at 4.2 K and 23 T, showing a practical range of current carrying capacities. The maximum J(c), 4900 A/mm(2) (I-c = 550 A), was observed for a 55-filament tape at 4.2 K and 0 T. A single pancake coil using 3.5 m long tape generated a maximum magnetic field of 1.9 T, showing a possibility for realizing over ST-class coils.

引用

页码：248 / 251

页数：4

共 50 条

[1] Transport properties of Bi-2212/Ag multifilamentary composite tape in high magnetic fields
Hitachi Ltd, Ibaraki, Japan
Phys B Condens Matter, 3-4 (248-251):
[2] Fabrication of laminated Bi-2212/Ag multifilamentary tape
Yuan, DW
Majer, WJ
Francavilla, TL
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (03): : 287 - 290
[3] Transport properties of Bi-2212/Ag multifilamentary tape under a large electromagnetic stress state
Wakuda, T
Okada, M
Awaji, S
Watanabe, K
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 952 - 955
[4] Fabrication and transport properties of Bi-2212/Ag multifilamentary tapes and coils for high magnetic field generation
Okada, M
Fukushima, K
Sato, J
Nomura, K
Kitaguchi, H
Kumakura, H
Kiyoshi, T
Togano, K
Wada, H
APPLIED SUPERCONDUCTIVITY 1997, VOLS 1 AND 2: VOL 1: SMALL SCALE AND ELECTRONIC APPLICATIONS; VOL 2: LARGE SCALE AND POWER APPLICATIONS, 1997, (158): : 1599 - 1602
[5] Processing and superconducting properties of the butt-joint of Bi-2212/Ag multifilamentary tape
Okada, Michiya
Fukushima, Keiji
Tanaka, Kazuhide
Hirano, Tatsumi
Sato, Junichi
Kitaguchi, Hitoshi
Kumakura, Hiroaki
Togano, Kazumasa
Wada, Hitoshi
Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 1997, 61 (09): : 849 - 855
[6] Processing and superconducting properties of the butt-joint of Bi-2212/Ag multifilamentary tape
Okada, M
Fukushima, K
Tanaka, K
Hirano, T
Sato, J
Kitaguchi, H
Kumakura, H
Togano, K
Wada, H
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1997, 61 (09) : 849 - 855
[7] Bi-2212 phase formation process in multifilamentary Bi-2212/Ag wires and tapes
Koizumi, T
Hasegawa, T
Nishioka, J
Hikichi, Y
Nakatsu, T
Kumakura, H
Kitaguchi, I
Matsumoto, A
Nagaya, S
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 2538 - 2541
[8] Fabrication and transport properties of Bi-2212/Ag multifilamentary coils for high magnetic field generation (II); high field performance test
Kitaguchi, H
Kumakura, H
Togano, K
Okada, M
Tanaka, K
Fukushima, K
Nomura, K
Sato, J
APPLIED SUPERCONDUCTIVITY 1997, VOLS 1 AND 2: VOL 1: SMALL SCALE AND ELECTRONIC APPLICATIONS; VOL 2: LARGE SCALE AND POWER APPLICATIONS, 1997, (158): : 1543 - 1546
[9] Anomaly in J(c)-B hysteresis for Bi-2212/Ag composite tape in high field
Kitaguchi, H
Kumakura, H
Togano, K
APPLIED SUPERCONDUCTIVITY, 1995, 3 (11-12) : 535 - 541
[10] Bi-2212/Ag Tape Conductor and Coil Development
Albert, G. W.
Zhou, R.
Leung, E. M.
Salazar, K. V.
Advances in Cryogenic Engineering, (41/A):

← 1 2 3 4 5 →