Mechanical properties of underwater friction stir welded 2219 aluminum alloy

被引：111
|
作者：
Liu Hui-jie [1 ]
Zhang Hui-jie [1 ]
Huang Yong-xian [1 ]
Yu Lei [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2010年 / 20卷 / 08期
关键词：
aluminum alloy; underwater friction stir welding; mechanical property; MICROSTRUCTURE; PRECIPITATION;
D O I：
10.1016/S1003-6326(09)60309-5
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history. The results indicated that the tensile strength of the joint can be improved from 324 MPa by external water cooling action in normal to 341 MPa. However, the plasticity of the joint is deteriorated. The underwater joint tends to fracture at the interface between the weld nugget zone and the thermal mechanically affected zone on the advancing side during tensile test, which is significantly different from the normal joint.
引用
下载
收藏
页码：1387 / 1391
页数：5
相关论文
共 50 条
  • [1] Mechanical properties of underwater friction stir welded 2219 aluminum alloy
    刘会杰
    张会杰
    黄永宪
    于雷
    Transactions of Nonferrous Metals Society of China, 2010, 20 (08) : 1387 - 1391
  • [2] Homogeneity of Mechanical Properties of Underwater Friction Stir Welded 2219-T6 Aluminum Alloy
    Liu, H. J.
    Zhang, H. J.
    Yu, L.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2011, 20 (08) : 1419 - 1422
  • [3] Homogeneity of Mechanical Properties of Underwater Friction Stir Welded 2219-T6 Aluminum Alloy
    H. J. Liu
    H. J. Zhang
    L. Yu
    Journal of Materials Engineering and Performance, 2011, 20 : 1419 - 1422
  • [4] Effect of welding speed on microstructures and mechanical properties of underwater friction stir welded 2219 aluminum alloy
    Liu, H. J.
    Zhang, H. J.
    Yu, L.
    MATERIALS & DESIGN, 2011, 32 (03): : 1548 - 1553
  • [5] Mechanical properties of electric assisted friction stir welded 2219 aluminum alloy
    Chen, Shujun
    Zhang, Hongwei
    Jiang, Xiaoqing
    Yuan, Tao
    Han, Yang
    Li, Xiaoxu
    JOURNAL OF MANUFACTURING PROCESSES, 2019, 44 : 197 - 206
  • [6] Microstructure and mechanical properties of 2219 aluminum alloy refilling friction stir welded joints
    Lu, H. (luhao@sjtu.edu.cn), 1600, Harbin Research Institute of Welding (34):
  • [7] Microstructure and Mechanical Properties of 2219-T Aluminum Alloy Welded by Friction Stir Welding
    Dong, Feng-bo
    Guo, Li-jie
    Luo, Chuan-hong
    Wei, Xiang-fu
    INTERNATIONAL CONFERENCE ON APPLIED MECHANICS AND MECHANICAL AUTOMATION (AMMA 2017), 2017, : 1 - 5
  • [8] Microstructures and mechanical properties of friction stir welded 2219-T87 aluminum alloy joints
    Wang, Chunyan
    Qu, Wenqing
    Yao, Junshan
    Zhao, Haiyun
    Hanjie Xuebao/Transactions of the China Welding Institution, 2010, 31 (10): : 77 - 80
  • [9] Microstructure and mechanical properties of friction stir welded joints in 2219-T6 aluminum alloy
    Xu, Weifeng
    Liu, Jinhe
    Luan, Guohong
    Dong, Chunlin
    MATERIALS & DESIGN, 2009, 30 (09) : 3460 - 3467
  • [10] Effect of cold spraying on residual stress and mechanical properties of friction stir welded 2219 aluminum alloy joint
    Zhiwei Q.
    Xiawei Y.
    Yangfan Z.
    Huawei T.
    Wenya L.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2022, 43 (06): : 82 - 87
12345