Effect of surface macroroughness on the microstructure and sliding wear properties of Al2O3+13 wt.% TiO2 thick coatings

被引：0
|
作者：
Zesati-Belmontes, Sara I. [1 ,2 ]
Lopez-Baltazar, Enrique A. [2 ]
Ruiz-Mondragon, Jose J. [3 ]
Ruiz-Luna, Haidee [2 ,4 ]
Alvarado-Hernandez, Francisco [2 ]
Baltazar-Hernandez, Victor H. [2 ]
机构：
[1] CIATEQ, Manufactura Avanzada Sede Aguascalientes, Aguascalientes 20358, Mexico
[2] Univ Autonoma Zacatecas, Mat Sci & Engn Program, Zacatecas 98000, Mexico
[3] Corp Mexicana Invest Mat SA CV, Coahuila 25290, Mexico
[4] Univ Autonoma Zacatecas, CONACYT, Zacatecas 98000, Mexico
来源：
REVISTA DE METALURGIA | 2022年 / 58卷 / 04期
关键词：
-% TiO2 coatings; Macroroughness; Sliding wear; Thermal spraying; Thick coating; MECHANICAL-PROPERTIES; PLASMA SPRAY; RESISTANCE; ROUGHNESS; SUBSTRATE; BEHAVIOR;
D O I：
10.3989/revmetalm.232
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Two macro-roughness patterns namely spiral grooving and diamond knurling were performed on an AISI/SAE 1045 cylindrical steel bar. Al2O3 + 13 wt.-% TiO2 powder was deposited by utilizing a multi-pass torch. Microstructure, microhardness and wear resistance were analyzed. The presence of both gamma-Al2O3 and alpha-Al2O3 throughout the coating was promoted by partially melted and un-melted particles; however, the formation of interlayers of hard alpha-Al2O3 was influenced by the re-heating during the multi-pass torch causing transformation from gamma-Al2O3 ->alpha-Al2O3. Knurling pattern specimens contained less defects owe to a suitable splat accommodation thus strengthening the inter-splat anchorage. The improved sliding wear resistance was influenced by both the combination of gamma-Al2O3 (toughness) and alpha-Al2O3 (hardness) phases and, predominantly by the reduced porosity and micro-cracks in specimens with the knurling pattern.
引用
收藏
页数：9
相关论文
共 50 条
  • [1] Surface remelting treatment of plasma-sprayed Al2O3+13 wt.% TiO2 coatings
    Iwaszko, Jozef
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (06): : 3443 - 3451
  • [2] The Influence of Injection Mode and Spray Distance on Wear Resistance of Al2O3+13 wt.% TiO2 coatings
    Platek, Karolina
    Latka, Leszek
    Nowakowska, Monika
    ADVANCES IN MATERIALS SCIENCE, 2024, 24 (03): : 5 - 17
  • [3] The Microstructure and Selected Mechanical Properties of Al2O3+13 wt % TiO2 Plasma Sprayed Coatings
    Michalak, Monika
    Latka, Leszek
    Sokolowski, Pawel
    Niemiec, Aneta
    Ambroziak, Andrzej
    COATINGS, 2020, 10 (02)
  • [4] Microstructure evolution of laser remelted Al2O3-13 wt.%TiO2 coatings
    Li, C. G.
    Yu, Z. S.
    Zhang, Y. F.
    Zhang, P. L.
    Yan, H.
    Lu, Q. H.
    Li, W. G.
    Wang, Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 576 : 187 - 194
  • [5] Interfacial phenomena in the plasma spraying Al2O3+13 wt.% TiO2 ceramic coating
    Yang, YZ
    Liu, ZG
    Liu, ZY
    Chuang, YZ
    THIN SOLID FILMS, 2001, 388 (1-2) : 208 - 212
  • [6] Friction and wear behaviors of Al2O3-13 wt% TiO2 coatings
    Lin Lu
    Zhuang Ma
    Fu-Chi Wang
    Yan-Bo Liu
    Rare Metals, 2013, 32 (01) : 87 - 92
  • [7] Friction and wear behaviors of Al2O3-13 wt%TiO2 coatings
    Lu, Lin
    Ma, Zhuang
    Wang, Fu-Chi
    Liu, Yan-Bo
    RARE METALS, 2013, 32 (01) : 87 - 92
  • [8] Friction and wear behaviors of Al2O3–13 wt%TiO2 coatings
    Lin Lu
    Zhuang Ma
    Fu-Chi Wang
    Yan-Bo Liu
    Rare Metals, 2013, 32 : 87 - 92
  • [9] Influences of laser remelting on microstructure of nanostructured Al2O3-13 wt.% TiO2 coatings fabricated by plasma spraying
    Wang, Dongsheng
    Tian, Zongjun
    Shen, Lida
    Liu, Zhidong
    Huang, Yinhui
    APPLIED SURFACE SCIENCE, 2009, 255 (08) : 4606 - 4610
  • [10] COMPARATIVE STUDY ON WEAR PERFORMANCE OF TRADITIONAL AND NANOSTRUCTURED Al2O3-13 wt. % TiO2 AIR PLASMA SPRAY COATINGS
    Yao, Sun-Hui
    CERAMICS-SILIKATY, 2015, 59 (01) : 59 - 63
12345