Size effects in interlaminar tensile and shear strength of unidirectional glass fibre epoxy

被引：45
|
作者：
Wisnom, MR
Jones, MI
机构：
[1] University of Bristol, Department of Aerospace Engineering, Queens Building, Bristol BS8 ITR, University Walk
来源：
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES | 1996年 / 15卷 / 01期
关键词：
size effect; interlaminar tension; interlaminar shear; curved beam bending; short beam shear; delamination; Weibull theory;
D O I：
10.1177/073168449601500101
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
Curved beams tested in four point bending were used to measure interlaminar tensile strength, and straight beams loaded in three point bending to measure interlaminar shear strength. Results from specimens of 16, 32 and 64 plies with all dimensions scaled showed significant size effects. The average interlaminar tensile strength dropped from 109 MPa for the smallest specimens to 61 MPa for the largest, whilst the interlaminar shear strength was reduced from 97 MPd to 85 MPa.
引用
收藏
页码：2 / 15
页数：14
相关论文
共 50 条
  • [1] Directional Interlaminar Shear Strength (ILSS) of nano-modified epoxy/unidirectional glass fibre composite
    Rajanish, M.
    Nanjundaradhya, N. V.
    Sharma, Ramesh S.
    Shivananda, H. K.
    Hegde, Alok
    [J]. AIMS MATERIALS SCIENCE, 2018, 5 (04) : 603 - 613
  • [2] Reduction in tensile and flexural strength of unidirectional glass fibre-epoxy with increasing specimen size
    Wisnom, MR
    Atkinson, JW
    [J]. COMPOSITE STRUCTURES, 1997, 38 (1-4) : 405 - 411
  • [3] Interlaminar tensile strength of carbon fibre-epoxy specimen size, layup and manufacturing effects
    Wisnom, MR
    Jones, MI
    Hill, GFJ
    [J]. ADVANCED COMPOSITES LETTERS, 2001, 10 (04) : 171 - 177
  • [4] Role of matrix modification on interlaminar shear strength of glass fibre/epoxy composites
    Liu, Yu
    Yang, Jiao-Ping
    Xiao, Hong-Mei
    Qu, Cheng-Bing
    Peng, Qing-Ping
    Fu, Shao-Yun
    Shindo, Yasuhide
    [J]. COMPOSITES PART B-ENGINEERING, 2012, 43 (01) : 95 - 98
  • [5] Influence of the manufacturing process on the interlaminar tensile strength of thick unidirectional continuous epoxy/carbon fibre composites
    Grabow, M.
    Keryvin, V
    Marchandise, A.
    Grandidier, J-C
    Baley, C.
    Le Guennec, C.
    Fagherazzi, O.
    [J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2022, 154
  • [6] EFFECT OF SPECIMEN SIZE ON INTERLAMINAR SHEAR-STRENGTH OF UNIDIRECTIONAL CARBON FIBER-EPOXY
    CUI, WC
    WISNOM, MR
    JONES, M
    [J]. COMPOSITES ENGINEERING, 1994, 4 (03): : 299 - 307
  • [7] Effect of graphene oxide size on interlaminar shear strength of glass fabric/epoxy composites
    Zeng, Xiao-Ling
    Tang, Bo-Lin
    Shen, Xiao-Jun
    Dang, Chen-Yang
    Shi, Yi-Cheng
    Feng, Ming-Jia
    Fu, Shao-Yun
    [J]. MATERIALS RESEARCH EXPRESS, 2019, 6 (10)
  • [8] Organoclay effect on transverse tensile strength and in-plane shear strength of unidirectional glass/epoxy nanocomposites
    Tsai, Jia-Lin
    Wu, Ming-Dao
    [J]. ADVANCES IN COMPOSITE MATERIALS AND STRUCTURES, PTS 1 AND 2, 2007, 334-335 : 773 - +
  • [9] Effect of matrix modification on interlaminar shear strength of glass fibre reinforced epoxy composites at cryogenic temperature
    Wu, Zhixiong
    Li, Jingwen
    Huang, Chuanjun
    Li, Laifeng
    [J]. PROCEEDINGS OF THE 25TH INTERNATIONAL CRYOGENIC ENGINEERING CONFERENCE AND INTERNATIONAL CRYOGENIC MATERIALS CONFERENCE 2014, 2015, 67 : 1068 - 1073
  • [10] The interlaminar shear strength test of helical wound glass fibre reinforced epoxy laminates subjected to hydrothermal ageing
    Majid, M. S. Abdul
    Afendi, M.
    Daud, R.
    Amin, N. A. M.
    Mohamad, A.
    Hekman, M.
    [J]. MECHANICAL AND MATERIALS ENGINEERING, 2014, 554 : 391 - +
12345