Hydrophobicity, water moisture transfer and breathability of PTFE-coated viscose fabrics prepared by electrospraying technology and sintering process

被引：17

作者：

Yang, Kai ^{[1
]}

Peng, Qingyan ^{[1
]}

Venkataraman, Mohanapriya ^{[1
]}

Novotna, Jana ^{[1
]}

Karpiskova, Jana ^{[2
]}

Mullerova, Jana ^{[2
]}

Wiener, Jakub ^{[1
]}

Vikova, Martina ^{[1
]}

Zhu, Guocheng ^{[3
]}

Yao, Juming ^{[4
,5
]}

Militky, Jiri ^{[1
]}

机构：

[1] Tech Univ Liberec, Fac Text Engn, Dept Mat Engn, Liberec, Czech Republic

[2] Tech Univ Liberec, Inst Nanomat Adv Technol & Innovat, Dept Nanochem, Liberec, Czech Republic

[3] Zhejiang Sci Tech Univ, Coll Text Sci & Engn, Xiasha Educ Pk, Hangzhou, Peoples R China

[4] Zhejiang Sci Tech Univ, Sch Mat Sci & Engn, Xiasha Educ Pk, Hangzhou, Peoples R China

[5] Ningbo Univ, Sch Mat Sci & Chem Engn, Ningbo, Peoples R China

来源：

PROGRESS IN ORGANIC COATINGS | 2022年 / 165卷

关键词：

PTFE; Viscose fabric; Electrospraying; Sintering; Hydrophobic; Janus fabric; COTTON; FUNCTIONALIZATION; SEPARATION; MEMBRANES; TEXTILES; BEHAVIOR; POLYMER;

D O I：

10.1016/j.porgcoat.2022.106775

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

Coating of PTFE on the fabrics is one facial method to obtain the hydrophobic/superhydrophobic property. However, the breathability of the PTFE-coated fabrics prepared by traditional methods (e.g., sputtering) is significantly affected. Electrospraying technology was able to create the pure PTFE coating layer on any sub-strates and the following sintering process is necessary to obtain the hydrophobic/superhydrophobic property. In this work, the PTFE-coated viscose fabrics were firstly prepared via electrospraying technology and then stabi-lized after 10 min sintering process with different temperatures ranging from 150 degrees C to 210 degrees C. The morphology, hydrophobicity, breathability, and water moisture transfer of the PTFE-coated viscose fabrics as well as the chemical compatibility between PTFE microparticles and viscose fabric were investigated. With increased sin-tering temperature, the PTFE coating layer on the viscose fabric became physically denser, which corresponded to the reduced breathability. Only when sintering temperature was equal to or higher than 190 degrees C, the stable hydrophobicity of PTFE-coated viscose fabric was found. When sintering temperature was increased from 190 degrees C to 210 degrees C, the contact angle hysteresis of the hydrophobic PTFE-coated viscose fabric decreased from 9.2 degrees to 3.4 degrees and the one-way water moisture transfer was enhanced.

引用

页数：11