Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247

被引：36
|
作者：
Sulak, Ivo [1 ]
Obrtlik, Karel [1 ]
机构：
[1] Acad Sci Czech Republ, Inst Phys Mat, Zizkova 22, Brno 61662, Czech Republic
来源：
ENGINEERING FRACTURE MECHANICS | 2017年 / 185卷
关键词：
Nickel-based superalloy; High-temperature low-cycle fatigue; Tensile dwell; Fatigue life; Damage mechanisms; DAMAGE MECHANISMS; CREEP-FATIGUE; DEGREES-C; ALLOY; 713LC; LIFE;
D O I：
10.1016/j.engfracmech.2017.04.002
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Hot isostatically-pressed, nickel-based superalloy MAR-M247 was tested under fatigue and creep-fatigue conditions. Continuous cycling and cycling with 10 min tensile dwells in each cycle were applied in symmetrical strain control cycle with constant total strain amplitude at 900 degrees C in air. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained. The introduction of tensile dwells resulted in lower fatigue life in total strain representation. Surface relief, specimen sections and fracture surface observations revealed crack initiation sites, crack density and crack paths, and help to clarify the effect of dwells on fatigue behaviour. (C) 2017 Elsevier Ltd. All rights reserved.
引用
下载
收藏
页码：92 / 100
页数：9
相关论文
共 50 条
  • [1] High-temperature low-cycle fatigue behaviour of HIP treated and untreated superalloy MAR-M247
    Sulak, I.
    Obrtlik, K.
    Celko, L.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2016, 54 (06): : 471 - 481
  • [2] HIGH-TEMPERATURE LOW-CYCLE FATIGUE AND CYCLIC CONSTITUTIVE RELATION OF MAR-M247 DIRECTIONALLY SOLIDIFIED SUPERALLOY
    HASEBE, T
    SAKANE, M
    OHNAMI, M
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1992, 114 (02): : 162 - 168
  • [3] High-Temperature Low-Cycle Fatigue Behaviour of MAR-M247 Coated with Newly Developed Thermal and Environmental Barrier Coating
    Sulak, Ivo
    Obrtlik, Karel
    Celko, Ladislav
    Gejdos, Pavel
    Jech, David
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2018, 2018
  • [4] LOW CYCLE FATIGUE BEHAVIOUR AND FATIGUE CRACK INITIATION IN MAR-M247 AT 700 °C
    Sulak, Ivo
    Obrtlik, Karel
    Hrbacek, Karel
    METAL 2017: 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2017, : 1580 - 1586
  • [5] Investigation of fatigue crack incubation and growth in cast MAR-M247 subjected to low cycle fatigue at room temperature
    Yeratapally, Saikumar R.
    Hochhalter, Jacob D.
    Ruggles, Timothy J.
    Sangid, Michael D.
    INTERNATIONAL JOURNAL OF FRACTURE, 2017, 208 (1-2) : 79 - 96
  • [6] Investigation of fatigue crack incubation and growth in cast MAR-M247 subjected to low cycle fatigue at room temperature
    Saikumar R. Yeratapally
    Jacob D. Hochhalter
    Timothy J. Ruggles
    Michael D. Sangid
    International Journal of Fracture, 2017, 208 : 79 - 96
  • [7] Effect of Aluminide Coating Thickness on High-Temperature Fatigue Response of MAR-M247 Nickel-Based Superalloy
    Kopec, Mateusz
    COATINGS, 2024, 14 (08)
  • [8] The low cycle fatigue behaviour of MAR-M247 superalloy under different strain rates and cycle shapes at 750?C
    Sulak, I.
    Obrtlik, K.
    Babinsky, T.
    Guth, S.
    INTERNATIONAL JOURNAL OF FATIGUE, 2022, 164
  • [9] EFFECT OF HIP ON LOW CYCLE FATIGUE OF MAR-M247 AT 900°C
    Sulak, Ivo
    Obrtlik, Karel
    Skorik, Viktor
    Hrbacek, Karel
    METAL 2014: 23RD INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2014, : 1381 - 1386
  • [10] Creep behaviour and life assessment of a cast nickel - base superalloy MAR-M247
    Kvapilova, Marie
    Dvorak, Jiri
    Kral, Petr
    Hrbacek, Karel
    Sklenicka, Vaclav
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2019, 38 (01) : 590 - 600
12345