Thermal conductivities of (U, Pu, Am)O2 solid solutions
被引:30
|作者:
Morimoto, Kyoichi
[1
]
Kato, Masato
[1
]
Ogasawara, Masahiro
[2
]
Kashintura, Motoaki
[1
]
Abe, Tomoyuki
[1
]
机构:
[1] Japan Atom Energy Agcy, Naka, Ibaraki 3191194, Japan
[2] Inspect Dev Co, Naka, Ibaraki 3191194, Japan
关键词:
actinide alloys and compounds;
ceramics;
thermodynamic properties;
D O I:
10.1016/j.jallcom.2006.12.159
中图分类号:
O64 [物理化学(理论化学)、化学物理学];
学科分类号:
070304 ;
081704 ;
摘要:
The thermal conductivities of (U0.7-zPu0.3Amz)O-2 solid solutions (z = 0.007-0.03) were studied by the laser flash method at temperatures from 900 to 1773 K. First, the thermal conductivities of (U0.68Pu0.3Am0.02)O-2 solid solutions were measured as a function of density (rho = 85-95% of theoretical density). The dependence of the thermal conductivities on the effective porosity (1 - rho) was evaluated by the correction equations of Loeb, Maxwell-Eucken and Shultz, and then the experimental values were best-fitted with the correction coefficient of beta=0.5 in the Maxwell-Eucken equation. The thermal conductivities of (U0.7-zPu0.3Amz)O-2 solid solutions were found to decrease slightly with increasing Am-content. The thermal conductivities satisfied the classical phonon transport model, lambda = (A + BT)(-1) up to about 1500 K. The coefficient A increased linearly with increasing Am-content, and little variation was observed in the coefficient B. The dependencies of the coefficients A and B on the Am-content were evaluated by the phonon scattering model. The coefficients obtained in the experiment could be theoretically well explained, assuming that the chemical formula of Am-MOX was U(0.7-2z)4+Uz5+Pu0.34+Amz3+O22- (C) 2007 Elsevier B.V. All rights reserved.