Comparison of microstructure and magnetic properties of 3% Si-steel, amorphous and nanostructure Finemet

被引：4
|
作者：
Yousefi, M. [1 ]
Rahmani, Kh. [1 ]
Kerahroodi, M. S. Amiri [1 ]
机构：
[1] Shahid Beheshti Univ, Power & Water Coll Engn, Energy & Mech Engn Dept, POB 16765-1719, Tehran, Iran
来源：
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS | 2016年 / 420卷
关键词：
Finemet; 3%Si-steel; Microstructure and hysteresis; NANOCRYSTALLIZATION; PERMEABILITY; ALLOY; PHASE;
D O I：
10.1016/j.jmmm.2016.07.015
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This paper presents a comparison of microstructure and magnetic properties of polycrystalline 3%Sisteel, amorphous and nano-crystalline alloy Fe(735)Cu(1)Nb(3)Sii(35)B(9) (known as Finemet). Si-steels are industrially produced by casting, hot and cold rolling, annealing and coating. Samples of thin amorphous ribbons were prepared by the planar flow casting (PFC) method. Nano-crystalline samples are obtained after annealing in vacuum furnace at 560 degrees C for 1 h. The structure of specimens was investigated by XRD, SEM and FE-SEM. Also, magnetic properties were measured using vibrating sample magnetometer (VSM). The results showed that, hysteresis losses in as-quenched and nano-crystalline ribbons were by 94.75% and 96.06% less than 3%Si-steel, respectively. After the heat treatment of amorphous specimens, hysteresis area was decreased by 25% in comparison with heat treated specimen. This decreasing is occurred due to the formation of Fe3Si nanostructure with size of 10-17 nm and removing segregation after heat treatment. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：204 / 209
页数：6
相关论文
共 50 条
  • [1] Microstructure and magnetic properties of FINEMET nanowires
    Lupu, N. (nicole@phys-iasi.ro), 1600, American Institute of Physics Inc. (113):
  • [2] Microstructure and magnetic properties of FINEMET nanowires
    Chiriac, H.
    Corodeanu, S.
    Ovari, T. -A.
    Lupu, N.
    JOURNAL OF APPLIED PHYSICS, 2013, 113 (17)
  • [3] Nanostructure and magnetic properties of Ni-substituted finemet ribbons
    Iturriza, N.
    Fernandez, L.
    Ipatov, M.
    Vara, G.
    Pierna, A. R.
    del Val, J. J.
    Chizhik, A.
    Gonzalez, J.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 316 (02) : E74 - E77
  • [4] Effects of chemical composition on nanocrystallization kinetics, microstructure and magnetic properties of finemet-type amorphous alloys
    Shivaee, Hossein Asghari
    Castellero, Alberto
    Rizzi, Paola
    Tiberto, Paola
    Hosseini, Hamid Reza Madaah
    Baricco, Marcello
    METALS AND MATERIALS INTERNATIONAL, 2013, 19 (04) : 643 - 649
  • [5] Effects of chemical composition on nanocrystallization kinetics, microstructure and magnetic properties of finemet-type amorphous alloys
    Hossein Asghari Shivaee
    Alberto Castellero
    Paola Rizzi
    Paola Tiberto
    Hamid Reza Madaah Hosseini
    Marcello Baricco
    Metals and Materials International, 2013, 19 : 643 - 649
  • [6] Observation of secondary recrystallization process in 3% Si-steel with EBSD
    Komatsubara, M
    Imamura, T
    TEXTURES OF MATERIALS, PTS 1 AND 2, 2002, 408-4 : 1323 - 1328
  • [7] Mo-containing Finemet alloys: microstructure and magnetic properties
    Franco, V
    Conde, CF
    Conde, A
    Ochin, P
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2001, 287 (1-3) : 366 - 369
  • [8] FINEMET type alloy without Si: Structural and magnetic properties
    Muraca, D.
    Cremaschi, V.
    Moya, J.
    Sirkin, H.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2008, 320 (09) : 1639 - 1644
  • [9] The effect of mechanical milling on the soft magnetic properties of amorphous FINEMET alloy
    Gheiratmand, T.
    Hosseini, H. R. Madaah
    Davami, P.
    Gjoka, M.
    Song, M.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2015, 381 : 322 - 327
  • [10] Microscale texture of hot deformed 3%Si-steel and statically recrystallized orientations
    Muraki, M
    Ozaki, Y
    Obara, T
    Komatsubara, M
    TEXTURES OF MATERIALS, PTS 1 AND 2, 2002, 408-4 : 1317 - 1322
12345