Preparation and characterization of NASICON material by sol-gel method

被引：0
|
作者：
Zhang, S
Quan, BF [1 ]
Zhao, ZY
Zou, YC
He, YH
Chen, LH
机构：
[1] Jilin Univ, Inst Elect Sci & Engn, Changchun 130023, Peoples R China
[2] Jilin Univ, State Key Lab Inorgan Synth & Preparat Chem, Changchun 130023, Peoples R China
来源：
CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE | 2003年 / 24卷 / 08期
关键词：
solid electrolyte; NASICON; sol-gel method; CO2-sensor;
D O I：
暂无
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Solid electrolyte. NASICON material hag been synthesized by, Sol-Gel method. The structure and composition were determined, by XRD, IR Absorption spectra, Raman spectra and NMR. The. superionic electric characteristic was determined by conductivity measurement. The experimental results show that the powders sintered at 900 degreesC possess better properties compared with those of the samples sintered at 700, 800 and 1 100 degreesC.
引用
收藏
页码：1356 / 1359
页数：4
相关论文
共 11 条
  • [1] Conductivity measurements on nasicon and nasicon-modified materials
    Bohnke, O
    Ronchetti, S
    Mazza, D
    [J]. SOLID STATE IONICS, 1999, 122 (1-4) : 127 - 136
  • [2] CATION VIBRATIONS IN INORGANIC OXIDE GLASSES
    EXARHOS, GJ
    RISEN, WM
    [J]. SOLID STATE COMMUNICATIONS, 1972, 11 (05) : 755 - &
  • [3] Gong J, 2002, CHEM J CHINESE U, V23, P102
  • [4] NASICON thick film-based CO2 sensor prepared by a sol-gel method
    Kida, T
    Miyachi, Y
    Shimanoe, K
    Yamazoe, N
    [J]. SENSORS AND ACTUATORS B-CHEMICAL, 2001, 80 (01) : 28 - 32
  • [5] NMR study of sol-gel processed NASICON
    Licoccia, S
    Di Vona, ML
    Traversa, E
    Montanaro, L
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (6-7) : 925 - 929
  • [6] Liu W, 2001, CHEM J CHINESE U, V22, P16
  • [7] NAKMOTO K, 1986, INFRARED RAMAN SPECT, P134
  • [8] QUAN BF, 2002, J TRANSDUCER TECHNOL, V21, P11
  • [9] Rao KJ, 2001, P INDIAN AS-CHEM SCI, V113, P497
  • [10] Sol-gel processing of NASICON thin film using aqueous complex precursor
    Shimizu, Y
    Ushijima, T
    [J]. SOLID STATE IONICS, 2000, 132 (1-2) : 143 - 148
12