Fabrication and mechanical properties of lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere

被引：2

作者：

Kashihara, Makoto ^{[1
]}

Yonetani, Hirosi ^{[1
]}

Kobi, Takahiro ^{[1
]}

Hyun, Soong-Keun ^{[2
]}

Suzuki, Shinsuke ^{[2
]}

Nakajima, Hideo ^{[2
]}

机构：

[1] Mori Seiki Co Ltd, Iga 5191414, Japan

[2] Osaka Univ, Inst Sci & Ind Res, Suita, Osaka 565, Japan

来源：

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 2008年 / 94卷 / 01期

关键词：

lotus-type porous carbon steel; nitrogen; porous metals; porosity; unidirectional solidification; tensile test;

D O I：

10.2355/tetsutohagane.94.30

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Lotus-type porous carbon steel (AISI1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 mu m s(-1). Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.

引用

页码：30 / 34

页数：5

共 50 条

[1] Fabrication of lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere
Kashihara, M
Hyun, SK
Yonetani, H
Kobi, T
Nakajima, H
SCRIPTA MATERIALIA, 2006, 54 (04) : 509 - 512
[2] Fabrication of lotus-type porous stainless steel by unidirectional solidification under hydrogen atmosphere
Ikeda, T
Tsukamoto, M
Nakajima, H
MATERIALS TRANSACTIONS, 2002, 43 (11) : 2678 - 2684
[3] Fabrication of Lotus-type Porous Silicon by Unidirectional Solidification in Pressurized Hydrogen Atmosphere
Yang, Qiandian
Liu, Yuan
Li, Yanxiang
MATERIALS PERFORMANCE, MODELING AND SIMULATION, 2013, 749 : 217 - 222
[4] Fabrication of lotus-type porous silicon by unidirectional solidification in hydrogen
Nakahata, T
Nakajima, H
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 384 (1-2): : 373 - 376
[5] Fabrication of Lotus-Type Porous Carbon Steel Slabs by Continuous Casting Technique in Nitrogen Atmosphere
Makoto Kashihara
Shinsuke Suzuki
Yuki Kawamura
Sang-Youl Kim
Hiroshi Yonetani
Hideo Nakajima
Metallurgical and Materials Transactions A, 2010, 41 : 2377 - 2382
[6] Fabrication of Lotus-type Porous Carbon-steel by Continuous Casting Technique in Nitrogen Atmosphere
Kashihara, M.
Yonetani, H.
Suzuki, S.
Hyun, S. K.
Kim, S. Y.
Kawamura, Y.
Nakajima, H.
POROUS METALS AND METALLIC FOAMS: METFOAM 2007, 2008, : 201 - +
[7] Fabrication of Lotus-Type Porous Carbon Steel Slabs by Continuous Casting Technique in Nitrogen Atmosphere
Kashihara, Makoto
Suzuki, Shinsuke
Kawamura, Yuki
Kim, Sang-Youl
Yonetani, Hiroshi
Nakajima, Hideo
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (09): : 2377 - 2382
[8] Fabrication of lotus-type porous copper-aluminum alloy by unidirectional solidification in hydrogen atmosphere
Hyun, Soong-Keun
Awadu, Tsuyoshi
Ikeda, Teruyuki
Nakajima, Hideo
THERMEC 2006, PTS 1-5, 2007, 539-543 : 1898 - +
[9] Fabrication of lotus-type porous magnesium and its alloys by unidirectional solidification under hydrogen atmosphere+
Hoshiyama, H.
Ikeda, T.
Nakajima, H.
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2007, 26 (04) : 303 - 316
[10] Fabrication of lotus-type porous magnesium and its alloys by unidirectional solidification under hydrogen atmosphere+
Institute of Scientific and Industrial Research, Osaka University, Ibaraki, Osaka 567-0047, Japan
不详
不详
High Temp Mater Processes, 2007, 4 (303-316):

← 1 2 3 4 5 →