Adsorption of Lead and Nickel on to Expanded Graphite Decorated with Manganese Oxide Nanoparticles

In this study, expanded graphite (EG) was decorated with manganese oxide nanoparticles (MONPs) by the hydrothermal method, and the newly formed composite (MONPs-EG) was applied as adsorbent for the removal of heavy metals from aqueous solutions. The comparative and competitive adsorption of Pb2+ and Ni2+ (0.01-1.00 mM) on MONPs-EG was investigated. Data from isothermal adsorption of single and binary systems suggested that both Pb2+ and Ni2+ were well described by the Langmuir isotherm, and the maximum adsorption capacities at 298 K were calculated at 0.278 and 0.113 mmol/g for Pb2+ and Ni2+, respectively. In binary systems, a dramatic decrease in adsorption capacity of Ni2+ was observed, while the adsorption capacity of Pb2+ was almost stable, indicating the favorable adsorption of Pb2+ over Ni2+ onto the prepared adsorbent. Kinetics studies of single and binary systems showed that a pseudo-second order model could explain the adsorption processes well. Thermodynamic analysis results demonstrated that the adsorption of these metal ions on the prepared adsorbent is spontaneous and exothermic in nature. The adsorption capacity of MONPs-EG increased significantly in the presence of humic acids. Overall, the results of this study suggest that MONPs-EG can be used effectively as an adsorbent for heavy metals removal from aqueous solutions.