Synthesis and properties of cubic zirconia-alumina composite by mechanical alloying

被引：55
|
作者：
Kwon, NH
Kim, GH
Song, HS
Lee, HL
机构：
[1] Korea Inst Sci & Technol, Ceram Proc Res Ctr, Seoul 130650, South Korea
[2] Yonsei Univ, Dept Ceram Engn, Seodaemoon Ku, Seoul 120749, South Korea
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2001年 / 299卷 / 1-2期
关键词：
mechanical alloying; solid electrolyte; cubic zirconia; alumina; precipitation; sintering;
D O I：
10.1016/S0921-5093(00)01376-9
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Synthesis of 8mol%Y2O3-ZrO2 (8YSZ) powder with Al2O3 by mechanical alloying (MA) and the sintering behavior of this powder were investigated. The solubility of Al2O3 in 8YSZ was 1.15 wt.% after MA for 48 h. Large agglomerated particles formed during MA resulted in a slow densification rate of the compact. After eliminating the agglomerates by sedimentation, the relative density of 97% was obtained by sintering the compact at 1400 degreesC for 2 h. Sintered microstructure of mechanically alloyed 3wt.%Al2O3-8YSZ (3A8YSZ) consisted of 8YSZ grains in the size range of 0.5-1.2 mum and 20-400 nm size Al2O3 particles dispersed uniformly in the 8YSZ. Fracture toughness and hardness of the composite was improved due to intragranular dispersion of Al2O3 particles. Electrical conductivity of the composite was 6.4 x 10(-5) S cm(-1) at 400 degreesC and also exhibited significant increase over monolithic 8YSZ. Improvement in lattice conductivity was unique in this composite and attributed to the role of intragranular Al2O3 particles, which provided strong lattice distortion of 8YSZ matrix. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：185 / 194
页数：10
相关论文
共 50 条
  • [1] MECHANICAL-PROPERTIES OF ZIRCONIA-ALUMINA WHISKER COMPOSITE CERAMICS
    TAMARI, N
    TANAKA, T
    KONDOH, I
    KOSE, S
    GOTOH, K
    NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1992, 100 (04): : 613 - 616
  • [2] COMBUSTION SYNTHESIS AND PROPERTIES OF ZIRCONIA-ALUMINA POWDERS
    DHAS, NA
    PATIL, KC
    CERAMICS INTERNATIONAL, 1994, 20 (01) : 57 - 66
  • [3] Study on mechanical properties of Zirconia-Alumina based ceramics
    Markandan, Kalaimani
    Chin, Jit Kai
    Tan, Michelle T. T.
    PROCESS AND ADVANCED MATERIALS ENGINEERING, 2014, 625 : 81 - 84
  • [4] Relationship of microstructure to mechanical and thermal properties of zirconia-alumina composites
    Zárate, J
    Contreras, ME
    Juárez, H
    Pérez, R
    REVISTA MEXICANA DE FISICA, 2004, 50 : 54 - 56
  • [5] Low-temperature processing and mechanical properties of zirconia and zirconia-alumina nanoceramics
    Vasylkiv, O
    Sakka, Y
    Skorokhod, VV
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2003, 86 (02) : 299 - 304
  • [6] Electrical properties of zirconia-alumina composites
    M'Peko, JC
    Spavieri, DL
    da Silva, CL
    Fortulan, CA
    de Souza, DPF
    de Souza, MF
    SOLID STATE IONICS, 2003, 156 (1-2) : 59 - 69
  • [7] Synthesis and sintering characteristics of zirconia and zirconia-alumina nanocomposites
    Prabhu, GB
    Bourell, DL
    NANOSTRUCTURED MATERIALS, 1995, 6 (1-4): : 361 - 364
  • [8] Mechanical and tribological properties of injection molded zirconia-alumina for orthopedic implants
    Terrizzi, Anna Rita
    Fersini, Maurizio
    Contaldi, Vincenzo
    Padmanabhan, Sanosh Kunjalukkal
    Einarsrud, Mari -Ann
    Licciulli, Antonio
    CERAMICS INTERNATIONAL, 2022, 48 (21) : 31211 - 31222
  • [9] Lifetime estimation of a zirconia-alumina composite for biomedical applications
    Fabbri, Paride
    Piconi, Corrado
    Burresi, Emiliano
    Magnani, Giuseppe
    Mazzanti, Francesca
    Mingazzini, Claudio
    DENTAL MATERIALS, 2014, 30 (02) : 138 - 142
  • [10] Synthesis and characterization of zirconia-alumina mixed oxides
    Dumeignil, F
    Blanchard, P
    Payen, E
    Grimblot, J
    Poulet, O
    HYDROTREATMENT AND HYDROCRACKING OF OIL FRACTIONS, 1997, 106 : 547 - 560
12345