Sulfate Ions Immobilization of Calcined Layered Double Hydroxides in Hardened Cement Paste and Concrete

被引：6
|
作者：
Ma Juntao [1 ,2 ,4 ]
Wang Daguang [2 ]
Duan Ping [3 ,4 ]
Shi Yanke [1 ,2 ]
机构：
[1] Yellow River Inst Hydraul Res, MWR Ctr Levee Safety & Dis Prevent, Zhengzhou 450003, Peoples R China
[2] North China Univ Water Resources & Elect Power, Int Joint Res Lab Ecobldg Mat & Engn Henan, Zhengzhou 450045, Peoples R China
[3] China Univ Geosci, Fac Mat Sci & Chem, Minist Educ, Engn Res Ctr Nanogeomat, Wuhan 430074, Peoples R China
[4] Wuhan Univ Technol, State Key Lab Silicate Mat Architectures, Wuhan 430070, Peoples R China
来源：
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2019年 / 34卷 / 06期
基金：
中国国家自然科学基金;
关键词：
calcined layered double hydroxides (CLDHs); sulfate ions; immobilization; hardened cement paste; HYDROTALCITE; ADSORPTION;
D O I：
10.1007/s11595-019-2205-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The sulfate ions immobilization behavior of calcined layered double hydroxides (CLDHs) in the hardened cement paste was investigated. The experimental results show that the sulfate ions in cement paste are immobilized by CLDHs to reconstruct the layered structure and aggregate around CLDHs. The immobilization amount of sulfate ions by CLDHs reaches 4.74x10(-3) mol/g, while the increasing amount indicates non-linear relation with the addition of CLDHs. The incorporation of CLDHs decreases the amount of ettringite formed to limit the expansion of cement paste, which decays the sulfate reaction to enhance the sulfate resistance of concrete.
引用
收藏
页码：1400 / 1407
页数：8
相关论文
共 50 条
  • [1] Sulfate Ions Immobilization of Calcined Layered Double Hydroxides in Hardened Cement Paste and Concrete
    马军涛
    WANG Daguang
    段平
    SHI Yanke
    [J]. Journal of Wuhan University of Technology(Materials Science), 2019, 34 (06) : 1400 - 1407
  • [2] Sulfate Ions Immobilization of Calcined Layered Double Hydroxides in Hardened Cement Paste and Concrete
    Juntao Ma
    Daguang Wang
    Ping Duan
    Yanke Shi
    [J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2019, 34 : 1400 - 1407
  • [3] Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste
    Yoon, Seyoon
    Moon, Juhyuk
    Bae, Sungchul
    Duan, Xiaonan
    Giannelis, Emmanuel P.
    Monteiro, Paulo M.
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2014, 145 (03) : 376 - 386
  • [4] Immobilization of Penicillin G Acylase on Calcined Layered Double Hydroxides
    Evans D.G.
    [J]. Chemical Research in Chinese Universities, 2003, (03) : 324 - 329
  • [5] Immobilization of penicillin G acylase on calcined layered double hydroxides
    Ren, LL
    He, J
    Evans, DG
    Duan, X
    [J]. CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2003, 19 (03) : 324 - 329
  • [6] Effect of Layered Double Hydroxides on the Deterioration Process of Cement Paste under Sulfate Attack
    Zhang, Lei
    Jiang, Linhua
    Zhi, Fangfang
    Jiang, Chunmeng
    Jin, Weizhun
    Yang, Guohui
    Chen, Cheng
    Zhang, Jianfeng
    [J]. MATERIALS, 2022, 15 (23)
  • [7] Characterization and adaptability of layered double hydroxides in cement paste
    Yang, Lei
    Zhao, Piqi
    Liang, Chen
    Chen, Mingxu
    Niu, Liyue
    Xu, Jun
    Sun, Dengtian
    Lu, Lingchao
    [J]. APPLIED CLAY SCIENCE, 2021, 211
  • [8] Research on the Carbonation of Cement Paste Modified with Layered Double Hydroxides
    Chen, Liangjun
    Chen, Xiaoxing
    Chen, Wei
    [J]. ADVANCED BUILDING MATERIALS AND SUSTAINABLE ARCHITECTURE, PTS 1-4, 2012, 174-177 : 706 - 710
  • [9] SULFATE ATTACK ON HARDENED CEMENT PASTE
    WANG, JG
    [J]. CEMENT AND CONCRETE RESEARCH, 1994, 24 (04) : 735 - 742
  • [10] Calcined layered double hydroxides as a "biomolecular vessel" for bromelain: Immobilization, storage and release
    Shi, Wenying
    Wei, Min
    Jin, Lan
    Li, Congju
    [J]. JOURNAL OF MOLECULAR CATALYSIS B-ENZYMATIC, 2007, 47 (1-2) : 58 - 65
12345