Zinc wetting during hot dip galvanising

被引：7
|
作者：
Bordignon, L.
Vanden Eynde, X.
机构：
[1] CRM
来源：
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES | 2007年 / 104卷 / 06期
关键词：
Annealing - Galvanizing - Oxygen - Partial pressure - Steel - Surface analysis - Wetting;
D O I：
10.1051/metal:2007119
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The meniscograph and the sessile drop wetting methods, associated with in situ surface analyses, were used to quantify the influence of the annealing atmosphere on zinc wetting during the hot dip galvanising of high strength steels. If a clear wetting improvement is obtained for higher oxygen partial pressures, associated with a sufficient hydrogen amount, in the soaking area, a dry atmosphere above the zinc bath has however to be preferred.
引用
收藏
页码：300 / 307
页数：8
相关论文
共 50 条
  • [1] Study of growth mechanism of zinc hot dip galvanising coatings
    Pistofidis, N.
    Chaliampalias, D.
    Vourlias, G.
    SURFACE ENGINEERING, 2009, 25 (08) : 594 - 596
  • [2] The Effect of Ductile Cast Iron Matrix on Zinc Coating During Hot Dip Galvanising of Castings
    Kopycinski, D.
    Szczesny, A.
    ARCHIVES OF FOUNDRY ENGINEERING, 2012, 12 (04) : 101 - 104
  • [3] HOT DIP GALVANISING FOR POWER PYLONS
    不详
    ANTI-CORROSION METHODS AND MATERIALS, 1971, 18 (12) : 5 - &
  • [4] Environmental advances in hot dip galvanising
    Industrial Galvanizers Corp, Girraween
    Process and Control Engineering, 1995, 48 (03):
  • [5] HOT DIP GALVANISING AT EBBW VALE
    不详
    METALLURGIA, 1969, 79 (474): : 145 - &
  • [6] Damage caused by hot dip galvanising
    Zgraggen, M
    Winkler, R
    Winkler, M
    Germ, H
    Trüllinger, S
    Faller, M
    von Trzebiatowski, O
    PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2006, 43 (04): : 184 - 191
  • [7] Hot Dip Galvanising Awards 2002
    不详
    ANTI-CORROSION METHODS AND MATERIALS, 2002, 49 (06) : 446 - 448
  • [8] Emission control for hot dip galvanising
    Product Finishing (London), 1996, 49 (01):
  • [9] Plunger for hot dip galvanising plants
    Zaccheroni, Giulio
    Wire Industry, 1993, 60 (709): : 33 - 34
  • [10] Modelling of iron dissolution during hot dip galvanising of strip steel
    O'Dell, S
    Charles, J
    Vlot, M
    Randle, V
    MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (02) : 251 - 256
12345