Preparation of mesoporous silica from rice husk ash: effect of depolymerizing agents on physico-chemical properties

被引:6
|
作者
Suttiruengwong, S. [1 ,2 ,3 ]
Puathawee, P. [1 ]
Chareonpanich, M.
机构
[1] Silpakorn Univ, Fac Engn & Ind Technol, Dept Mat Sci & Engn, Nahkon Pathom 73000, Thailand
[2] Chulalongkorn Univ, Ctr Excellence Petr Petrochem & Adv Mat, Bangkok 10330, Thailand
[3] Kasetsart Univ, Fac Engn, Dept Chem Engn, Bangkok 10900, Thailand
来源
关键词
mesoporous silica; rice husk ash; depolymerizing agent; hydrophobicity;
D O I
10.4028/www.scientific.net/AMR.93-94.664
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The aim of this work was to prepare mesoporous silicas derived from rice husk ash (RHA) using three different depolymerizing agents; glycerol, 1,3 propanediol and 1,4 butanediol. The reaction of RI-TA with different depolymerizing agents was carried out between 200-250 degrees C for 2 hrs. The solution was then hydrolyzed with deionized water to obtain gels. After a few washing step, gels were oven-dried and calcined at 500 degrees C for 24 hrs. Prepared mesoporous silicas were then characterized using Nitrogen adsorption-desorption measurement, FTIR, TGA, SEM, XRD and XRF. The percent hydrophobicity was determined based on the amount of moisture absorbed using TGA. It was shown that RHA reacted with depolymerizing agents above 200 degrees C to form gels, which, after hydrolysis and calcination, still maintained the mesoporous characteristics. The BET and SEM results indicated that the RHA reacted with 1,3 propanediol had highest pore volume (0.95 cm(3)/g) and specific surface area (129.30 m(2)/g) compared to RHA reacted with glycerol and 1,4 butanediol. The distribution of pores computed from BJH desorption branch was also more uniform. FTIR indicated that there was no significant change in the chemical structure of RHA reacted with different depolymerizing agents. The residual C-H bands were found in FTIR spectra for all prepared mesoporous silicas. TGA thermograms confirmed the existence of organic residues (below 2 %wt), which might result from incomplete elimination even after calcination. This was found to be an important factor affecting the hydrophobic property of the reacted RHA. The hydrophobicity of RHA may be tailored by controlling depolymerizing agents and organic residues. Depolymerizing agents with longer carbon chains also favoured the hydrophobic characteristics.
引用
收藏
页码:664 / +
页数:2
相关论文
共 50 条
  • [1] Mesoporous Silica from Rice Husk Ash
    Shelke, V. R.
    Bhagade, S. S.
    Mandavgane, S. A.
    BULLETIN OF CHEMICAL REACTION ENGINEERING AND CATALYSIS, 2010, 5 (02): : 63 - 67
  • [2] Preparation and antibacterial activity of mesoporous silica based on rice husk ash
    Zhang, Dong-Dong
    Hu, Si
    Pan, Peng-Yun
    Zhang, Min
    Wu, Qiong
    Zhang, Yu-Rong
    Zhou, Xian-Qing
    LWT-FOOD SCIENCE AND TECHNOLOGY, 2023, 185
  • [3] Preparation and properties of rice husk ash silica filled natural rubber
    Zhang, Guojie
    Wang, Ge
    Jiang, Yang
    Wang, Shifeng
    Zhang, Yong
    POLYMER COMPOSITES, 2024, 45 (01) : 438 - 447
  • [4] Green Synthesis of Crystalline Silica from Sugarcane Bagasse Ash: Physico-Chemical Properties
    Seroka, Ntalane S.
    Taziwa, Raymond
    Khotseng, Lindiwe
    NANOMATERIALS, 2022, 12 (13)
  • [5] Effect of silica forms in rice husk ash on the properties of concrete
    Le Anh-tuan Bui
    Chun-tsun Chen
    Chao-lung Hwang
    InternationalJournalofMineralsMetallurgyandMaterials, 2012, 19 (03) : 252 - 258
  • [6] Effect of silica forms in rice husk ash on the properties of concrete
    Le Anh-tuan Bui
    Chun-tsun Chen
    Chao-lung Hwang
    Wei-sheng Wu
    International Journal of Minerals, Metallurgy, and Materials, 2012, 19 : 252 - 258
  • [7] Effect of silica forms in rice husk ash on the properties of concrete
    Le Anh-tuan Bui
    Chen, Chun-tsun
    Hwang, Chao-lung
    Wu, Wei-sheng
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2012, 19 (03) : 252 - 258
  • [8] Synthesis and Characterization of Bimodal Mesoporous Silica Derived from Rice Husk Ash
    Watthanachai, Chanyarak
    Ngamcharussrivichai, Chawalit
    Pengprecha, Somchai
    ENGINEERING JOURNAL-THAILAND, 2019, 23 (01): : 25 - 34
  • [9] Simultaneous preparation of silica and activated carbon from rice husk ash
    Liu, Yan
    Guo, Yupeng
    Gao, Wei
    Wang, Zhuo
    Ma, Yuejia
    Wang, Zichen
    JOURNAL OF CLEANER PRODUCTION, 2012, 32 : 204 - 209
  • [10] PROPERTIES OF SILICA FROM RICE HUSK AND RICE HUSK ASH AND THEIR UTILIZATION FOR ZEOLITE Y SYNTHESIS
    Saceda, Jan-Jezreel F.
    de Leon, Rizalinda L.
    Rintramee, Kamolwan
    Prayoonpokarach, Sanchai
    Wittayakun, Jatuporn
    QUIMICA NOVA, 2011, 34 (08): : 1394 - U289