ISOTHERMAL STABILITY AND SELECTED MECHANICAL PROPERTIES OF Zr48Cu36Al8Ag8 BULK METALLIC GLASS

被引：7
|
作者：
Blyskun, P. [1 ]
Latuch, J. [1 ]
Kulik, T. [1 ]
机构：
[1] Warsaw Univ Technol, Fac Mat Sci & Engn, 141 Woloska Str, PL-02507 Warsaw, Poland
来源：
ARCHIVES OF METALLURGY AND MATERIALS | 2017年 / 62卷 / 03期
关键词：
bulk metallic glasses; isothermal stability; mechanical properties; TTT curve; FORMING ABILITY; ALLOY;
D O I：
10.1515/amm-2017-0266
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The aim of this work was to investigate the influence of isothermal annealing on the amorphous structure stability of the Zr48Cu36Al8Ag8 alloy. A series of continuous heating examinations was performed on the differential scanning calorimeter in order to determine the temperature limits for isothermal annealing series where the time to crystallization was measured. The obtained results were calculated and a time-temperature-transformation diagram was created and discussed. Static compression test as well as microhardness measurements of the as-quenched samples gave a mechanical properties results supplement. The measured properties (sigma(c) = 1800 MPa and 614 HV0.05) are comparable to the literature results for this alloy. Fractographic observations with the scanning electron microscope were also performed in order to prove some plasticity observed during the strength tests.
引用
收藏
页码：1749 / 1753
页数：5
相关论文
共 50 条
  • [1] Synthesis of Bulk Zr48Cu36Al8Ag8 Metallic Glass by Hot Pressing of Amorphous Powders
    He, Tianbing
    Ciftci, Nevaf
    Uhlenwinkel, Volker
    Scudino, Sergio
    JOURNAL OF MANUFACTURING AND MATERIALS PROCESSING, 2021, 5 (01):
  • [2] In situ isothermal crystallisation of Zr48Cu36Al8Ag8 bulk metallic glass based on pair distribution function analyses
    Xu, Y.
    Fan, C.
    Lin, J. P.
    Ren, Y.
    Hao, G. J.
    Chen, G. L.
    MATERIALS RESEARCH INNOVATIONS, 2013, 17 : S89 - S93
  • [3] Overheating effects on thermal stability and mechanical properties of Cu36Zr48Ag8Al8 bulk metallic glass
    Zhao, Yanchun
    Kou, Shengzhong
    Suo, Hongli
    Wang, Renjun
    Ding, Yutian
    MATERIALS & DESIGN, 2010, 31 (02) : 1029 - 1032
  • [4] Effect of Overheated Level on Thermal Stability and Mechanical Properties of Cu36Zr48Ag8Al8 Bulk Metallic Glass
    Zhao Yanchun
    Kou Shengzhong
    Wang Renjun
    Suo Hongli
    Ding Yutian
    Li Na
    Xue Shuwei
    Liu Guangqiao
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 (01) : 173 - 176
  • [5] Surface Modification of Zr48Cu36Al8Ag8 Bulk Metallic Glass through Glow Discharge Plasma Nitriding
    Kulikowski, Krzysztof
    Blyskun, Piotr
    Borowski, Tomasz
    Kulik, Tadeusz
    MATERIALS, 2024, 17 (12)
  • [6] Low-temperature glow discharge plasma oxidation of the Zr48Cu36Al8Ag8 bulk metallic glass
    K. Kulikowski
    P. Błyskun
    T. Kulik
    Archives of Civil and Mechanical Engineering, 24
  • [7] Low-temperature glow discharge plasma oxidation of the Zr48Cu36Al8Ag8 bulk metallic glass
    Kulikowski, K.
    Blyskun, P.
    Kulik, T.
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2024, 24 (02)
  • [8] Combined effect of isothermal annealing and pre-compression on mechanical properties of Cu36Zr48Al8Ag8 bulk metallic glass
    Gu, Ji
    Zhang, Li-xin
    Wang, Yi-han
    Ni, Song
    Guo, Sheng-feng
    Song, Min
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (06) : 1620 - 1628
  • [9] Effect of substituting elements on glass-forming ability of the new Zr48Cu36Al8Ag8 bulk metallic glass-forming alloy
    Zhang, Q. S.
    Zhang, W.
    Louzguine-Luzgin, D. V.
    Inoue, A.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 504 : S18 - S21
  • [10] Self-repair by stress-induced diffusion of noble elements during oxidation of Zr48Cu36Al8Ag8 bulk metallic glass
    Haratian, Saber
    Grumsen, Flemming B.
    Villa, Matteo
    Christiansen, Thomas L.
    Somers, Marcel A. J.
    SCRIPTA MATERIALIA, 2019, 164 : 126 - 129
12345