Templated mesoporous carbons and their performance for electric double layer capacitors

Templated mesoporous carbons with high surface area were successfully prepared by the carbonization of a mixture of thermoplastic precursor pitch with MgO precursors (magnesium acetate and citrate) at 950 degrees C in a N-2 atmosphere. The BET surface area of the carbons obtained reached a very high value without any activation process. The carbons were rich in mesopores. The electrochemical performance of mesoporous carbons prepared as electrode materials for electric double layer capacitors were also investigated. Measurement of capacitance was carried out in a mass fraction 30% KOH electrolyte. Results showed that the mesoporous carbons had a high specific capacitance and perfect rate performance. In particular, the sample prepared with a mass ratio of MgO to pitch of 4 for the magnesium citrate template showed a fairly high capacitance, about 284 F.g(-1) at a current density of 20 mA.g(-1) and 236 F.g(-1) at 1000 mA.g(-1). The impedance of all the capacitors was smaller than 3.5 Omega.