Alkali-Activated Phosphorous Slag Performance under Different Curing Conditions: Compressive Strength, Hydration Products, and Microstructure

被引：24

作者：

Maghsoodloorad, Hojjatollah ^{[1
]}

Khalili, Hamidreza ^{[2
]}

Allahverdi, Ali ^{[3
,4
]}

机构：

[1] Iran Univ Sci & Technol, Sch Chem Engn, Res Lab Inorgan Chem Proc Technol, Philosophy, Tehran 1684613114, Iran

[2] Iran Univ Sci & Technol, Sch Chem Engn, Res Lab Inorgan Chem Proc Technol, Sci, Tehran 1684613114, Iran

[3] Iran Univ Sci & Technol, Sch Chem Engn, Res Lab Inorgan Chem Proc Technol, Tehran 1684613114, Iran

[4] Iran Univ Sci & Technol, Cement Res Ctr, Tehran 1684613114, Iran

来源：

JOURNAL OF MATERIALS IN CIVIL ENGINEERING | 2018年 / 30卷 / 01期

关键词：

Phosphorous slag; Alkali activated; Curing conditions; Variance analysis; BLAST-FURNACE SLAG; NATURAL POZZOLAN; CEMENT; TEMPERATURE; ADMIXTURES; MIXTURES; KINETICS; CONCRETE; DOSAGE; WASTE;

D O I：

10.1061/(ASCE)MT.1943-5533.0002101

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In this paper, the impact of curing parameters such as precuring time, curing time, and temperature on compressive strength of mortar with phosphorous-slag cement activated with two different compound activators including NaOH+Na2CO3 and Na2CO3+Ca(OH)2, as well as the microstructure morphology of the hardened mortars, are studied. Furthermore, variance analysis is used to evaluate the effectiveness of each curing parameter. The results show that application of such a combined low-temperature and high-temperature curing regime can effectively improve the quality of the transition zone (porosity and bonding of the cement matrix to aggregate), in addition to the development of more polymeric structures (silicates of Q3-structures) in hydration products. These improvements together result in a threefold increase in the compressive strength compared with environmental curing conditions.

引用

页数：12

共 50 条

[1] Compressive Strength Performance of Alkali Activated Concretes under Different Curing Conditions
Nis, Anil
Altindal, Ilhan
[J]. PERIODICA POLYTECHNICA-CIVIL ENGINEERING, 2021, 65 (02): : 556 - 565
[2] Investigation of the relationship among the hydration, microstructure and compressive strength of alkali-activated phosphorus slag
Jia, Ruiquan
Wang, Qiang
Luo, Ting
[J]. JOURNAL OF BUILDING ENGINEERING, 2023, 76
[3] Influence of Different Curing Regimes on the Performance and Microstructure of Alkali-Activated Slag Concrete
El-Hassan, Hilal
Shehab, Ehab
Al-Sallamin, Abdelrahman
[J]. JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2018, 30 (09)
[4] HYDRATION PRODUCTS OF ALKALI-ACTIVATED SLAG CEMENT
WANG, SD
SCRIVENER, KL
[J]. CEMENT AND CONCRETE RESEARCH, 1995, 25 (03) : 561 - 571
[5] Compressive strength and microstructure of alkali-activated waste glass-slag cements
Menchaca-Ballinas, L. E.
Martinez-Lopez, R.
Escalante-Garcia, J., I
[J]. JOURNAL OF SUSTAINABLE CEMENT-BASED MATERIALS, 2023, 12 (04) : 381 - 392
[6] Alkali-activated slag: hydration process and development of microstructure
Wang, SD
[J]. ADVANCES IN CEMENT RESEARCH, 2000, 12 (04) : 163 - 172
[7] Alkali-activated fly ash/slag cement -: Strength behaviour and hydration products
Puertas, F
Martínez-Ramírez, S
Alonso, S
Vázquez, T
[J]. CEMENT AND CONCRETE RESEARCH, 2000, 30 (10) : 1625 - 1632
[8] Compressive Strength and Microstructure of Carbide Slag and Alkali-Activated Blast Furnace Slag Pastes in China
Li, Zhixin
Xu, Kaidong
Sun, Nan
Wang, Jina
Xue, Kaiwang
Xu, Longyun
Ren, Yi
Yan, Zhenzhou
Sima, Tongbao
[J]. BUILDINGS, 2024, 14 (06)
[9] Curing performance of alkali-activated cement-phosphorous slag and its compatibility with sulfur tailings
Jiang G.-Z.
Wu A.-X.
Wang Y.-M.
[J]. Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2020, 42 (08): : 963 - 971
[10] Compressive strength and microstructure of alkali-activated fly ash/slag binders at high temperature
Pan, Z.
Tao, Z.
Cao, Y. F.
Wuhrer, R.
Murphy, T.
[J]. CEMENT & CONCRETE COMPOSITES, 2018, 86 : 9 - 18

← 1 2 3 4 5 →