Pre-Oxidation Behavior of RE Modified HP40 Alloy

被引：0

作者：

Yan Jingbo ^{[1
]}

Gao Yimin

Shen Yudi ^{[2
]}

Liang Long

Ye Zhaozhong

Yi Dawei

Du Yingqian

Yao Caiying

机构：

[1] Xi An Jiao Tong Univ, Sch Mat Sci & Engn, State Key Lab Mech Behav Mat, Xian 710049, Peoples R China

[2] China Natl Heavy Machinery Res Inst Co Ltd, Xian 710032, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2011年 / 40卷

关键词：

acoustic-emission; rare earth; HP40; alloys; pre-oxidation; internal oxidation; OXIDATION BEHAVIOR; OXIDE; CARBURIZATION; THICKNESS; CORROSION; ELEMENTS; YTTRIUM; SILICON;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The oxide scale rupture behavior during cooling for the rare-earth modified HP40 alloy with different oxidation time was investigated by the acoustic-emission technology. The results show that the scale adherence is not improved obviously for the RE-modified alloy with 1 h pre-oxidation. However, the binding strength is increased with prolonging the oxidation time due to the internal oxidation caused by rare earth element. BSE experiment indicates the rare earth element facilitates the formation of internal oxide (silica), which changes the rupture behavior of the scale, thus improves the scale adherence.

引用

页码：491 / 494

页数：4

共 18 条

[1] Pre-oxidation of Inconel alloys for inhibition of carbon deposition from heated jet fuel
Altin, Orhan
Eser, Semih
[J]. OXIDATION OF METALS, 2006, 65 (1-2): : 75 - 99
[2] The stress and spalling behavior of the oxide scale formed on polycrystalline Ni3Al
Christensen, RJ
Lipkin, DM
Clarke, DR
[J]. ACTA MATERIALIA, 1996, 44 (09) : 3813 - 3821
[3] Douglass D.L., 1970, OXID MET, V2, P207
[4] CONDITIONS FOR THE INITIATION OF OXIDE SCALE CRACKING AND SPALLATION
EVANS, HE
LOBB, RC
[J]. CORROSION SCIENCE, 1984, 24 (03) : 209 - 222
[5] MODELING OXIDE SPALLATION
EVANS, HE
[J]. MATERIALS AT HIGH TEMPERATURES, 1994, 12 (2-3) : 219 - 227
[6] The effects of small additions of yttrium on the high-temperature oxidation resistance of a Si-containing austenitic stainless steel
Fujikawa, H
Morimoto, T
Nishiyama, Y
Newcomb, SB
[J]. OXIDATION OF METALS, 2003, 59 (1-2): : 23 - 40
[7] Microstructure of HK40 alloy after high-temperature service in oxidizing/carburizing environment - II. Carburization and carbide transformations
Kaya, AA
[J]. MATERIALS CHARACTERIZATION, 2002, 49 (01) : 23 - 34
[8] Structure and phase stability in a cast modified-HP austenite after long-term ageing
Kenik, EA
Maziasz, PJ
Swindeman, RW
Cervenka, J
May, D
[J]. SCRIPTA MATERIALIA, 2003, 49 (02) : 117 - 122
[9] Effects of silicon on the oxidation behavior of Ni-base chromia-forming alloys
Li, B.
Gleeson, B.
[J]. OXIDATION OF METALS, 2006, 65 (1-2): : 101 - 122
[10] Effects of minor elements on the cyclic-oxidation behavior of commercial Fe-base 800-series alloys
Li, B
Gleeson, B
[J]. OXIDATION OF METALS, 2004, 62 (1-2): : 45 - 69

← 1 2 →